炭素飽和溶鉄による CaO-SiO_2-Al_2O_3-TiO_2 系スラグ中の TiO_2 の還元速度

概要

論文の詳細を見る
Reduction rate of TiO_2 in CaO-SiO_2-Al_2O_3-TiO_2 slags by carbon dissolved in iron melts was investigated at 1350℃〜1600℃ under argon atmosphere. It was found that the reduction of TiO_2 proceeded simultaneusly with the reduction of SiO_2 and was promoted by the addition of silicon to the initial iron melts. For acid slags, the reduction rate of TiO_2 decreased with inceasing ratio of CaO/SiO_2, whereas it slightly increased for slags with CaO/SiO_2>1. The kinetic analysis on the basis of the two film theory showed that the overall rate of transfer of Ti from slag to metal phases was controlled by the rate of chemical reactions at the interface for cases without silicon addition, but it was found that the resistance to transfer of TiO_2 in the diffusion boundary layer at slag could not be neglected when some amount of silicon was added to the metal.
社団法人日本鉄鋼協会の論文
1988-11-01