溶鉄中のマンガンの Fe_tO(+MnO)-CaO(+MgO)-SiO_2 系スラグによる酸化速度

概要

論文の詳細を見る
The rate of oxidation of manganese in liquid iron by slag was investigated by measuring the change of manganese and oxygen contents of liquid iron covered with Fe_tO(+MnO)-CaO(+MgO)-SiO_2 slag in a magnesia crucible. Experiments were carried out with slags of basicity (=(CaO+MgO)/SiO_2) from 0.37 to 1.49 and Fe_tO content from 24 to 75 wt% at 1600℃. The oxidation reaction of manganese proceeded comparatively slowly except at the initial period and the equilibrium between liquid iron and slag was not attained within 60 min. The experimental results were interpreted by the rate equation derived from the assumption that the reaction rate was controlled by the transfer of Mn__-, O__-, (MnO) and (FeO) in the boundary layers and the driving force of the reaction varied with proceeding of the reaction. The effect of Fe_tO content of slag on the reaction rate was observed more clearly in the driving force than in the mass transfer coefficient. The effect of slag basicity on the reaction rate was not clear.
社団法人日本鉄鋼協会の論文
1981-01-01