溶鉄中の炭素によるスラグ中のシリカの還元速度

概要

論文の詳細を見る
The rate of reduction of silica in CaO-SiO_2 and CaO-Al_2O_3-SiO_2 slags by carbon in liquid iron was measured under various experimental conditions to examine effects of slag composition, temperature, atmosphere and slag graphite interfacial area. Effect of slag composition was ascribed to the change of activity of silica. Apparent activation energies were about 100kcal/mol for binary slags and 70-85kcal/mol for ternary slags. The rate of reduction increased linearly with the ratio of slag-graphite to slag-metal interfacial area in the low ratio region. It suggests that reaction of silica reduction proceeds electrochemically, and that interfacial reaction is the rate-determining step. The rate of reduction in argon atmosphere was about twice as fast as that in CO atmosphere.
社団法人日本鉄鋼協会の論文
1970-10-01