高炉・炉底部モデルによる耐火物の力学的挙動の検討

概要

論文の詳細を見る
To study the fracture mechanism of the refractories of blast furnace by thermal stress, a model furnace of hearth and bottom of Kakogawa No.2 B. F. was constructed. The model furnace was heated to about 1500℃, twice. Thermal stress (strain), displacement of refractories and those of shell were measured during the heating test. Crack behaviour of the refractories was detected by A. E. during the heating test and also by visual inspection after the test. The results are summarized as follows : 1. High stress was observed in refractories and in shell at the first heating test. The stress observed at the second heating test was less than that of the first. Also, displacement of shell and refractories was fairly affected by heat hysterisis. These phenomena may be caused mainly by irreversible shrinkage of joint mortal and carbon stamp. 2. Cracks were detected at side face of carbon blocks, by visual inspection. The result of A. E. signal indicated that these cracks probably occurred at the final stage of heating process of the first heating test.
社団法人日本鉄鋼協会の論文
1983-07-01