柱状晶-等軸晶遷移に及ぼす流動の影響
スポンサーリンク
概要
- 論文の詳細を見る
The effects of fluid flow and solidification conditions on the columnar-equiaxed transition are investigated. The ratio, R, of heat flux at dendrite tip to that at dendrite stem is introduced as a parameter which characterizes the columnar-equiaxed transition (For R>1, columnar grains grow, whereas for R<1, equiaxed grains grow). This heat flux ratio, R, is calculated for Fe-0.5%C alloy under varying condition by using the finite element method. The heat flux ratio thus calculated indicates, in good agreement with previously reported observation, that the columnar-equiaxed transition occurs when the temperature gradient decreases to about 5℃/cm under natural convective flow faster than 0.3cm/sec, and columnar grains come to grow again as the temperature gradient further decreases to less than 1℃/cm. For flow slower than 0.3cm/sec, only columnar grains are shown to grow.
- 社団法人日本鉄鋼協会の論文
- 1979-03-01
著者
-
佐々木 康
東京大学工学部:(現)pennsylvania大学
-
鈴木 俊夫
東京大学工学部
-
梅田 高照
東京大学工学部
-
木村 康夫
東京大学工学部
-
鈴木 俊夫
東京大学工学系大学院
-
木村 康夫
東海大学工学部金属材料工学科
関連論文
- TASCフォーラム 暗い日曜日--サブプライム・ローン問題寸感
- 電析デンドライトのフェーズフィールド解析
- Ag/Ag_2S系原子スイッチにおけるAg柱成長とスイッチング挙動の数値シミュレーション
- Si-45mass%Ni合金過冷融液表面のシリコンデンドライト成長(鋳造・凝固)
- Si-45mass%Ni合金融液からのシリコン結晶育成(鋳造・凝固)
- 凝固現象の基礎
- フェーズフィールドモデルにおける解析精度と計算効率
- 合金のデンドライト成長 : LKTモデルとフェーズフィールドモデル
- 3次元フェーズフィールドモデルによる合金デンドライト成長理論の検証
- 科学研究費補助金申請あれこれ