低質コークス使用によるキュポラ操業法に關する研究 IV
スポンサーリンク
概要
- 論文の詳細を見る
The main cause of deficiencies in a cupola operation followed by the use of low grade coke has been consumed as the reducing action of coke for CO_2 of furnace gas to CO. To prevent this undesirable action of low grade coke, the coating of coke with the calcium carbide slime was taken in the present study. I/2t cupola was operated by those coated coke. The effect of the coating on the reducing action of coke was investigated. Results obtained were summarized as follows : (1) The coating of coke with calcium-carbide slime shows a decreasing of the reducing action for CO_2 to CO. (2) The temperature of molten metal is rised 20∿50℃ by the coated coke. (3) CO_2% in the furnace gas taken at the top of cupola and the amount of coke consumption are lowered.
- 社団法人日本鉄鋼協会の論文
- 1948-11-25
著者
関連論文
- 第 49 回講演大會工場見学記
- クリープ試験方法規格原案 : 長時間クリープ試験法規格案(疲れおよびクリープ特集)
- 強じん鋳鉄について
- 客貨車平軸受用合金の軸受性能(潤滑油および潤滑特集)
- 鑄鐵のガス分析に就て
- 114 鑄鐵のガス分析について(日本鐵鋼協會第 45 回講演大會講演大要)
- 断熱材料
- 鑄物設計標準案(その1) : 金屬加工部門委員會第2回中間報告
- 電気爐による鑄鐵熔解法に關する研究
- 低質コークス使用によるキュポラ操業法に關する研究 IV
- 低質コークス使用によるキュポラ操業法に關する研究 (III)
- 低質コークス使用によるキュポラ操業法に關する研究 (II)
- 低質コークス使用によるキュポラ操業法に關する研究
- 31. 低質コークス使用によるキュポラ操業法に關する研究(第 2 報)
- 最近の疲労に関する諸問題
- 第1回ガスタービンに関する座談會記録 : 内燃機関部門主催
- 平和産業に對する材料
- 疲れ破壊の実例(疲れおよびクリープ特集)
- 34 鋲材の研究 : 普通鋼及び高張力鋼鋲材の製鋲及び〓鋲による材質的変化(日本鐵鋼協會第 50 回講演大会講演大要)
- 呉海軍工廠製鋼部の回顧(随想)(支部だより)
- 旧陸海軍鉄鋼技術調査委員会, 調査活動を終わる
- 国際交流委員会の活動状況
- 第二次世界大戦中における製鋼技術の開発研究
- 60 周年記念号「鉄鋼技術の進歩」の編集について
- 「最新溶接ハンドブック」, 増補版, 鈴木春義著, A5 版, 858 ページ, 定価 2, 800 円, 山海堂発行
- 128 古代鉄釘の冶金学的調査(低合金鋼ほか, 第 58 回講演大会講演大要)
- 114 Cu-P 系厚鋼板の材質について : 耐候性低合金の研究 II(性質一般・高マンガン鋼, 第 58 回講演大会講演大要)
- 113 鋼の耐候性におよぼす各種元素の影響 : 耐候性低合金鋼の研究 I(性質一般・高マンガン鋼, 第 58 回講演大会講演大要)
- 第 2 回世界冶金会議の鉄鋼精錬班に参加して(第 2 回世界冶金会議)