鑄鐵のガス分析に就て
スポンサーリンク
概要
- 論文の詳細を見る
A tentative model of gas-analysis equipment by vacuum-fusion method was developed with a view to investigate effects of the gas contained in the molten cast iron on the structure and character of cast iron product. Recurrence of analysis values was examined as to rimmed steel and cast iron. The following conclusions were obtained. 1) Recurrence of O_2 and N_2 analysis value for cast iron was somewhat lower than that for rimmed steel, the principal cause of difference being considered to be segregation of gas in analysis-specimens. 2) O_2 and N_2 contents of cast iron were both in the order of 0.00 χ wt% ; thus variations depending upon melting conditions could be detected by the proposed analysis method. 3) To secure higher reliability of gas analysis of cast iron, further studies should be carried out about the following points : a) To raise gas-extracting temperature. b) To improve the evacuating rate. c) To develop a sampling method with less segregation, etc.
- 社団法人日本鉄鋼協会の論文
- 1953-10-25
著者
関連論文
- クリープ試験方法規格原案 : 長時間クリープ試験法規格案(疲れおよびクリープ特集)
- 強じん鋳鉄について
- 客貨車平軸受用合金の軸受性能(潤滑油および潤滑特集)
- 鑄鐵のガス分析に就て
- 114 鑄鐵のガス分析について(日本鐵鋼協會第 45 回講演大會講演大要)
- 断熱材料
- 鑄物設計標準案(その1) : 金屬加工部門委員會第2回中間報告
- 電気爐による鑄鐵熔解法に關する研究
- 低質コークス使用によるキュポラ操業法に關する研究 IV
- 低質コークス使用によるキュポラ操業法に關する研究 (III)
- 低質コークス使用によるキュポラ操業法に關する研究 (II)
- 低質コークス使用によるキュポラ操業法に關する研究
- 31. 低質コークス使用によるキュポラ操業法に關する研究(第 2 報)
- 最近の疲労に関する諸問題
- 第1回ガスタービンに関する座談會記録 : 内燃機関部門主催
- 平和産業に對する材料
- 疲れ破壊の実例(疲れおよびクリープ特集)
- 第2回ガスタービンに関する座談會記録 : 内燃機関部門主催
- 炭化けい素質耐久鋳型によるブレーキディスク鋳造法