18Cr-12Ni 系耐熱鋼の高温強度におよぼす侵入型固溶元素間の相互作用の影響

概要

論文の詳細を見る
An investigation was made on the interactions induced by the simultaneous additions of interstitial solute elements such as C, N, and B, for the high temperature strength of 18 Cr-12 Ni heat resisting steel. The interactions were correlated with the age-hardening response, the softening characteristics after cold rolling and the structural change during creep. By the duplex additions of N and B, the obvious interaction that decreased the creep rupture strength lower than the sum of individual contributions was produced. This interaction was attributed in part to the strengthening of matrix more than the boundary due to precipitation hardening and in part to promoting the creep rupture by B addition in the coexistence with N. By the duplex additions of N and C, the deleterious interaction was also produced after prolonged time at 700℃. From these phenomena, the authors suggested a general condition for producing the interaction by the simultaneous additions of alloying elements for the high temperature strength.
社団法人日本鉄鋼協会の論文
1970-10-01