Behavior of CO_2 Absorption in Wet-grinding of Electronic Arc Furnace Reducing Slag by Vibration Ball Mill
スポンサーリンク
概要
- 論文の詳細を見る
A fundamental study was carried out in order to fix CO2 on slag. The electronic arc furnace reducing slag was wet-ground by a vibration ball mill under CO2 atmosphere. The effect of grinding conditions on the behavior of CO2 absorption was investigated.The rate of the absorption of CO2 under wet grinding was larger than that under dry grinding. The total amount of CO2 absorption increased with the increase in total amount of the slag and water in case that the weight ratio of the water to the slag was kept constant. The CO2 was fixed as CaCO3 and Ca4Si2O6(CO3)(OH, F)2. Any compounds of Mg were not detected by XRD after the experiment. In the early stage of grinding, the CO2 was absorbed even if the grinding was stopped. The concentration of Ca in the water was larger than the solubility of Ca(OH)2. Hence, the absorption of CO2 was determined by the surface reaction that consisted of chemical reaction and mass transfer in liquid. In the latter stage of grinding, the CO2 was not almost absorbed immediately after the grinding was stopped. The concentration of Ca in water was small. Accordingly, the absorption of CO2 was influenced by the dissolution of slag into water.The amount of the exhausted CO2 was calculated from the electronic power which was necessary for operating this experimental apparatus. The amount of CO2 absorption was larger than that of the exhausted CO2 from a solar, an atomic, a wind and a water power plant.
- 社団法人 日本鉄鋼協会の論文
- 2010-03-15
著者
-
UMEMOTO Minoru
Department of Production Systems Engineering, Toyohashi University of Technology
-
Umemoto Minoru
Department Of Production System Engineering Toyohashi University Of Technology
-
Umemoto Minoru
Department Of Production Systems Engineering Toyohashi University Of Technology
-
Bin Muhd
Department Of Mechanical And Manufacturing Engineering University Tun Hussein Onn Malaysia
-
YOKOYAMA Seiji
Department of Production Systems Engineering, Toyohashi University of Technology
-
SATO Ryousuke
Graduate School of Toyohashi University of Technology
-
Yokoyama Seiji
Department Of Production Systems Engineering Toyohashi University Of Technology
-
Umemoto Minoru
Department Of Mechanical Engineering Toyohashi University Of Technology
関連論文
- Heterogeneous Process of Disordering and Structural Refinement in Ni_3Al during Severe Plastic Deformation by High-Pressure Torsion
- Effect of Strain Path in High-Pressure Torsion Process on Hardening in Commercial Purity Titanium
- Influence of High-Pressure Torsion Straining Conditions on Microstructure Evolution in Commercial Purity Aluminum
- Phase Transformation and Magnetic Properties of Ferromagnetic Cu-Mn-Ga Alloys
- Formation of Surface Nanocrystalline Structure in Steels by Shot Peening and Role of Strain Gradient on Grain Refinement by Deformation
- Tribofilms Produced by Supply of Fine Metal Particles in Vacuum
- Phase Transformation and Magnetic Properties in Ni_Fe_xMn_Ga_ Alloys
- Structure Analysis of Coke, Wood Charcoal and Bamboo Charcoal by Raman Spectroscopy and Their Reaction Rate with CO_2
- Micro Pore Structure and Reaction Rate of Coke, Wood Charcoal and Graphite with CO_2
- Characterization of Relieved Non-metallic Inclusions in Stainless Steel by Image Processing of Micrographs
- Comparison of the Characteristics of Nanocrystalline Ferrite in Fe-0.89C Steels with Pearlite and Spheroidite Structure Produced by Ball Milling
- Serial Batch Elution of Electric Arc Furnace Oxidizing Slag Discharged from Normal Steelmaking Process into Fresh Water
- Behavior of CO_2 Absorption in Wet-grinding of Electronic Arc Furnace Reducing Slag by Vibration Ball Mill
- Formation and Annealing Behavior of Nanocrystalline Steels Produced by Ball Drop Test
- Nanocrystallization of Steels by Severe Plastic Deformation
- Mechanism of Crystal Size Refinement and Metastable Phase Formation by Mechanical Alloying (高次制御材料-2-)
- Formation of Surface Nanocrystalline Structure in Steels by Shot Peening and Role of Strain Gradient on Grain Refinement by Deformation
- Thermoelectric Properties of Ca-Mg-Si Alloys
- Effect of Co and Ni on Martensitic Transformation and Magnetic Properties in Fe-Pd Ferromagnetic Shape Memory Alloys
- Nanocrystallization of Steels by Various Severe Plastic Deformation Processes
- Effect of Aluminum and Oxygen Content on Diffusivity of Aluminum in Molten Iron
- Formation of Nanocrystalline Structure at the Surface of Drill Hole in Steel
- Comparison of Nanocrystalline Surface Layer in Steels Formed by Air Blast and Ultrasonic Shot Peening
- Process of Nanocrystallization and Partial Amorphization by Cold Rolling in TiNi
- Synthesis of Ferrite Nanoparticles by Mechanochemical Processing Using a Ball Mill
- Phase Transformations and Magnetostriction in Ni-Mn-Ga Ferromagnetic Shape Memory Alloys
- Synthesis of Fe-Cu Nanoparticles by Mechanochemical Processing Using a Ball Mill
- Comparative Analysis of Plastic Flow and Grain Refinement in Pure Aluminium Subjected to Simple Shear-Based Severe Plastic Deformation Processing
- Dry Sliding Wear Properties of Sub-Microcrystalline Ultra-Low Carbon Steel Produced by High-Pressure Torsion Straining
- Formation of Nanocrystalline Structure in Steels by Air Blast Shot Peening
- Nanocrystallization in Fe-C Alloys by Ball Milling and Ball Drop Test
- Model for Predicting Phase Transformation and Yield Strength of Vanadium Microalloyed Carbon Steels
- Model for Predicting Phase Transformation and Yield Strength of Vanadium Microalloyed Carbon Steels
- An Effective and Economic Strategy to Restore Acidified Freshwater Ecosystems with Steel Industrial Byproducts