Nanocrystallization in Fe-C Alloys by Ball Milling and Ball Drop Test
スポンサーリンク
概要
- 論文の詳細を見る
Microstructural evolution and nanocrystallization in various carbon steels by ball milling and ball drop test has been studied. In ball milling, nanocrystallization was observed in all the carbon steels irrespective of the carbon content (up to 0.9 mass% C) or starting microstructure (ferrite, martensite, pearlite or spheroidite). In ball drop test, nanocrystallization was observed in high carbon steels or ultrafine grained low carbon steels. It is realized that high strength before ball drop test is required for the nanocrystallization. The nanocrystalline structure obtained by ball milling and ball drop test has similar microstructure with dark smooth contrast. The morphologies such as pearlite lamellar, spheroidite cementite, ferrite grain boundary disappeared by nanocrystallization. The boundary between the nanocrystalline and work-hardened regions is quite sharp. The hardness of the nanocrystalline region is about two times higher than that of work-hardened region. The annealing of nanocrystalline region shows substantially slow grain growth and re-precipitation of fine cementite. This annealing behavior is quite different from the work-hardened region which is characterized by recrystallization and fast grain growth.From the present study, it was confirmed that the nanocrystalline structure produced by ball milling and ball drop test has quite similar in structure, hardness and annealing behavior although the number of deformation applied is substantially different.
- 社団法人 日本鉄鋼協会の論文
- 2002-12-15
著者
-
土谷 浩一
豊橋技科大
-
Tsuchiya Koichi
Department Of Applied Physics Faculty Of Engineering Hokkaido University
-
Umemoto Minoru
Department Of Production System Engineering Toyohashi University Of Technology
-
Todaka Yoshikazu
Department Of Mechanical Engineering Toyohashi University Of Technology
関連論文
- 28aXQ-9 ホイスラー型強磁性合金Co_2MnGeの内殻吸収磁気円二色性II(放射光真空紫外分光・MCD・光電子分光)(領域5)
- 21pWA-8 ホイスラー型強磁性合金 Co_2MnGe の内殻吸収磁気円二色性
- TiNi系形状記憶合金の表層非晶質化/ナノ結晶化に与えるショットピーニング条件の影響
- 希少・有害元素代替のための3d多元系機能材料の開発研究
- Cu-Mn-Ga系強磁性合金の相変態と磁気特性
- 25aXQ-8 充填型ホイスラー合金Co_2MnGeの光電子分光(光電子分光・逆光電子分光,領域5(光物性))
- 特集「顕微鏡法による材料開発のための微細構造研究最前線(7)-3D/4Dイメージング-」特集企画にあたって
- ボールミルを用いたメカノケミカル法によるフェライトナノ粒子の作製
- Heterogeneous Process of Disordering and Structural Refinement in Ni_3Al during Severe Plastic Deformation by High-Pressure Torsion
- Effect of Nanocrystallization and Twinning on Hardness in Ni_3Al Deformed by High-Pressure Torsion