Influence of Phosphorus, Sulpher, and Oxygen on 65% Nitric Acid Corrosion Resistance of Super High-clean 316L Stainless Steel

概要

論文の詳細を見る
For the purpose to verify the effect of decreasing phosphorus on corrosion properties of stainless steels, corrosion resistant tests in 65% nitric acid solutions were carried out for super-low phosphorus content 316L type stainless steels which were manufactured by the cold crucible type levitation melting method using Ca–CaF2 flux for aiming at the dephosphorization. By decreasing phosphorus content in these steels from 0.026 to 0.0002 mass%, the corrosion rate in 65% nitric acid solutions decreased remarkably. Especially even under 0.001% phosphorus content, the improvement of corrosion resistance against nitric acid solution could be observed.As for the non-metallic tramp elements, there were linear relations between corrosion rate and the very small amount of sulfur and oxygen contents in the super-low phosphorus stainless steels containing under 0.0002 mass% phosphorus. So the super high purification of these elements is also very effective for the improvement of corrosion resistance against nitric acid solutions.It is known that the corrosion of austenitic stainless steels containing over 0.003 mass% phosphorus in nitric acid solutions is intergranular corrosion. In the present work, it was confirmed that the corrosion of super-low phosphorus content 316L type stainless steels even at 0.0002 mass% was not uniform corrosion but intergranular corrosion.
社団法人日本鉄鋼協会の論文
2006-04-15