Fe-Cr-Ni-C-Al系およびFe-Cr-Ni-C-Si系合金の磁気特性とミクロ組織に及ぼすAlと Siの影響

概要

論文の詳細を見る
The magnetic properties and microstructures of Fe-17.5mass%Cr-2.0mass%Ni-0.5mass%C-αmass%Al (α=0.04-2.38) and Fe-17.5mass%Cr-2.0mass%Ni-0.5mass%C-αmass%Si (α=0.18-1.94) alloys were investigated in order to develop a magnetic material exhibiting high electric resistivity and softmagnetism when annealed at low temperatures, and paramagnetism when dissolution treated at high temperature. The addition of Al or Si was effective in increasing the electric resistivity, and improving the softmagnetism of the alloys step-annealed at 1053K and 923K. The improvement of the softmagnetism was discussed from the increase in the transformation temperature and variation of the microstructures. In the lower Al or Si content (≦0.7% Al or 1.6% Si), the alloys consisted of (α+γ+M_<23>C_6) phases at 1053K, the first annealing temperature. The mole fraction of the γ phase decreased with increasing Al or Si content because of the increase in the A_<c1> temperature. This change caused the decrease in the dislocation density due to the γ→α' transformation, and resulted in the improvement of the softmagnetism. On the other hand, most of the alloys were transformed to the paramagnetic γ phase by dissolution treatment at 1473K. However, the higher Al content alloys (≧1.91% Al) consisted of (γ+α) phases, and exhibited higher relative permeability than the others. This phenomenon was also interpreted from the increase in the transformation temperature with increasing Al content.
社団法人日本鉄鋼協会の論文

Fe-Cr-Ni-C-Al系およびFe-Cr-Ni-C-Si系合金の磁気特性とミクロ組織に及ぼすAlと Siの影響

スポンサーリンク

概要

著者

関連論文

スポンサーリンク