Preparation and Electrochromism of RF-Sputtered TiO2 Films
スポンサーリンク
概要
- 論文の詳細を見る
Titanium oxide ( TiO2) thin films were prepared by rf-sputtering in an Ar/O2 atmosphere from a compressed powder TiO2 target and their electrochromic (EC) phenomena were investigated. Films prepared under the sputtering pressures of 1.3, 4.0 and 6.7 Pa were confirmed by X-ray diffraction to be in amorphous state, anatase form and rutile form, respectively. Amorphous and anatase films showed cathodic EC properties. The maximum value of coloration efficiency was 14 cm2/C for the amorphous films in an electrolyte solution of 1N HCl. AC conductance measurements were measured from 110 Hz to 100 kHz for various oxygen contents in the sputtering atmosphere. The ac conductance gradually decreased with increasing oxygen content in the region of up to 30% and was independent of oxygen content in the region of more than 30%. In the films prepared in the sputtering atmospheres of oxygen contents of less than 30%, electronic conduction is interpreted to occur due to lack of oxygen. In the films prepared in oxygen contents of 30% and more, on the other hand, only ionic conduction is considered to exist.
- Publication Office, Japanese Journal of Applied Physics, Faculty of Science, University of Tokyoの論文
- 1997-07-15
著者
-
KITAO Michihiko
Research Institute of Electronics, Shizuoka University
-
URABE Kazuo
Research Institute of Electronics, Shizuoka University
-
Urabe Kazuo
Research Institute Of Electronics Shizuoka University
-
Kitao Michihiko
Research Institute Of Electronics Shizuoka University
-
Oshima Yoshihiro
Research Institute Of Electronics Shizuoka University
関連論文
- Preparation and Electrochromic Properties of RF-Sputtered NiO_x Films Prepared in Ar / 0_2 / H_2 Atmosphere
- Electrochromic Absorption Spectra of Mo_cW_O_3 Films : A: Applications and Fundamentals
- Absorption Bands of Eleclrochemically-Colored Films of WO_3, MoO_3 and Mo_cW_O_3
- Electron Diffusion in Amorphous Tungsten Oxide Films
- The Effect of Cu Additive on A.C. Conductivity in a-As_2Se_3
- Effect of Silver Additive on Frequency-Dependent Conductivity of Amorphous As_2Se_3
- Preparation of As_2Se_3 Single Crystals
- Recombination Radiation as Possible Mechanism of Light Emission from Reverse-Biased p-n Junctions under Breakdown Condition
- Electrochromic Coloration of Sputtered Nickel Oxide Films by Injection of Anions (Br^- Ions)
- Preparation and Electrochromism of RF-Sputtered TiO2 Films
- Variation of Photoconductivity Spectra of Amorphous As_2Se_3 with Light Chopping Frequency
- Localized-State Distributions in Ag-Modified As_2Se_3 Glasses
- Long-Term Photocurrent Decay in Amorphous As_2Se_3 Doped with Ag and Cu
- Temperature Dependence of A.C. Conductivity in Glassy As_Se_Ag_x
- Ac Conductivity of Amorphous As_2Se_3