Highly Ordered Molecular Orientation in a Phthalocyanine Film Deposited on a Well-Polished Indium–Tin Oxide Substrate

概要

論文の詳細を見る
Metal-free phthalocyanine (H2Pc) was deposited on an indium–tin oxide (ITO) substrate with a pentacene buffer layer, and the effect of polishing of the ITO surface on the molecular orientation of H2Pc was studied. By rubbing the ITO surface 10,000 times with a plastic eraser, the average surface roughness of ITO was decreased to 1.0 nm from its initial value of 2.0 nm, and the ($31\bar{3}$) X-ray diffraction peak of $\alpha$-form H2Pc became significantly large. Rocking curves and optical absorption spectra indicated that, by polishing the ITO surface, the disorder in the orientation of the stacking axis ($b$-axis) of H2Pc was reduced. A Schottky barrier cell of H2Pc with a highly ordered molecular orientation showed a lower photovoltaic performance than that with a disordered orientation.
2010-08-25