Promotion of Bone Formation around Alendronate-immobilized Screw-Type Titanium Implants after Implantation into Rat Molar Tooth Sockets
スポンサーリンク
概要
- 論文の詳細を見る
The aim of this study was to evaluate the effects of alendronate immobilization on bone formation following the implantation of apatite-coated titanium implants in rats. Thin carbonate-containing apatite coatings were deposited onto titanium implants (Ti implants) using a molecular precursor method. Alendronate was then immobilized on apatite-coated titanium implants (HA implants) by immersing the HA implants in alendronate solution (Ald implants). The rat molars were extracted, and the implants were immediately placed in the tooth sockets. Bone labeling was performed 14 and 7 days before sacrifice. At 3 and 9 weeks after implantation, undecalcified sections were prepared and bone histomorphometry was performed. Greater bone mass was found around the Ald implants than around either the Ti or HA implants at both 3 weeks and 9 weeks. At 3 weeks, fluorochrome bone labeling was greater around the Ald implants than around the Ti implants, and the values of bone to implant contact (BIC) and bone mass (BM) were significantly greater around the Ald implants than around the HA and Ti implants. At 9 weeks, bone labeling decreased and the values of BIC and BM increased compared with those at 3 weeks for all types of implant. In conclusion, we found that immobilized alendronate triggered pronounced bone formation around the implants at an early stage of bone healing. These results suggest that alendronate immobilization accelerates implant fixation early in the healing phase.
- 硬組織再生生物学会の論文
硬組織再生生物学会 | 論文
- BMPの臨床応用の問題点と解決
- ブタ顎関節関節円板、後部結合組織、下顎頭線維層におけるプロテオグリカンの比較検討
- 過酸化水素処理による骨芽細胞様細胞株MC3T3-E1のbone nodule形成への影響 : 石灰化物の結晶学的検索
- BMPを付与した電気化学的表面改質Ti及びHA-G-Ti複合材料の骨形成能
- 骨形成蛋白(BMP)の骨膜代用材としての応用 : ヒト大腿筋膜(SolVent Dehydrated Human Fascia Lata)との併用