Strategies for High Transparency Acrylate Resists for 157 nm Lithography
スポンサーリンク
概要
- 論文の詳細を見る
Several strategies were employed to improve the transparency and etch resistance of the acrylate-based 157 nm photoresists. (1) α-Fluorinated acrylates were synthesized and polymerized using radical initiation. The homopolymer of 2-[4-(2-hydroxy-hexafluoroisopropyl)cyclohexane]hexafluoro isopropyl-α-monofluoroacrylate (FA) showed high transparency at 157 nm (A = 1.7 μm<SUP>-1</SUP>), and its copolymer with norbornene hexafluoroalcohol and α-fluoro-tert-butylacrylate shows good 248 nm lithographic performance. (2) Selected acrylates containing hexafluoroisopropyl groups and hydrogenated single ring and multi-ring systems were prepared to address etch resistance. Homopolymers of acrylic versions of FA with different alicyclic moieties such as 1,3-cyclohexane, hydrogenated diphenyl ether and decaline showed very good transparency at 157 nm (A = 1.8 μm<SUP>-1</SUP>, 2.4 μm<SUP>-1</SUP>, 2.6 μm<SUP>-1</SUP>, respectively). T<SUB>g</SUB> values for these homopolymers were determined to be in the range of 91-95°C. (3) The POSS group was also used to improve etch resistance. POSS-containing non-fluorinated acrylate copolymers showed absorbances of 3.0-3.3 μm<SUP>-1</SUP> at 157 nm. POSS containing α-trifluoromethylacrylate polymers are expected to have lower absorbance. (4) To utilize an alternating copolymerization scheme, new fluorinated monomers containing both electron-rich and electron-deficient double bonds in one molecule were synthesized. The monomers were designed to undergo cyclopolymerization to generate polymers for improved transparency, etch resistance and outgassing properties.
- The Society of Photopolymer Science and Technology (SPST)の論文
The Society of Photopolymer Science and Technology (SPST) | 論文
- Influence of Solvent Vapor Atmospheres to the Self-assembly of Poly(styrene-b-dimethylsiloxane)
- Conventional Measurement Method of Film Resistance of Plasma-Polymerized Thin Films Using a High-Resistance Meter
- Synthesis and Optical Properties of Carbazole-Containing Donor-Acceptor Type Conjugated Polymers
- Novolak Resist Removal Using Laser (266/532nm)
- Evaluation of Fluorinated Diamond Like Carbon as Antisticking Layer by Scanning Probe Microscopy