Fabrication of the Electrode for Capacitor Cell Prepared by the Electrophoretic Deposition Method
スポンサーリンク
概要
- 論文の詳細を見る
A co-deposited film consisting of activated carbon (AC) and ketjenblack powder (KB) particles was prepared using the electrophoretic deposition (EPD) method and utilized as the electrode for a capacitor cell. As a result of evaluating various organic solvents as the dispersion solvent for the EPD bath, it was found that the best deposition condition was obtained using acetonitrile (AN). However, there was the problem that the co-deposited film consisting of AC and KB particles had a poor adhesion. The co-deposited film fabricated by adding polyvinylidine difluoride (PVdF) as a binder to the bath was able to be used as the electrode for a capacitor cell. The specific capacitance per unit weight of the electrode was almost equal to that of the commercial sheet electrode.
著者
-
UI Koichi
Faculty of Science & Technology, Tokyo University of Science
-
KOURA Nobuyuki
Faculty of Science & Technology, Tokyo University of Science
-
Okura Kazuma
Faculty Of Engineering The University Of Tokyo
-
KOURA Nobuyuki
Faculty of Science & Technology, Tokyo University of Science
-
OKURA Kazuma
Faculty of Science & Technology, Tokyo University of Science
-
TSUMEDA Satoru
Research Center, Nippon Chemi-con Corporation
-
TAMAMITSU Kenji
Research Center, Nippon Chemi-con Corporation
-
Tamamitsu Kenji
Research Center, Nippon Chem-Con Co.
関連論文
- 分散めっき法により作製したAg-TiO2(anatase)粒子分散膜の光触媒活性
- Electrochemical Behavior of Graphite-Lithium Intercalation Electrode in AlCl_3-EMIC-LiCl-SOCl_2 Room-Temperature Molten Salt
- Electrodeposition of Nb-Sn Alloy from SnCl2-NbCl5-EMIC Ambient Temperature Molten Salts (特集 New Trends in Molten Salt Chemistry and Electrochemistry)
- Experimental Design of a 32-bit Fully Asynchronous Microprocessor (FAM)
- Li二次電池用正極材料LiMn2-xMg04の熱力学的安定性と正極特性
- Fabrication of the Electrode for Capacitor Cell Prepared by the Electrophoretic Deposition Method
- 室温溶融塩からのアルミニウム-カーボンナノチューブ複合めっき
- Polyfluorene/Carbon Nanocomposite for Electrochemical Capacitors
- P44. Preparation of transparent nano-emulsion using tandem acoustic emulsification and its application to electropolymerization(Poster Presentation)