Internal fractures with the fish-eye were recognized in high cycle fatigue for Cr-Mo low alloy steel at elevated temperatures. To understand this phenomenon, the fish-eye patterns were examined in detail. Stepwise <I>S</I>-<I>N</I> curves were obtained for rotating bending and uniaxial loading fatigue tests and internal fractures with the fish-eye were observed at low stress and high cycle region. Stress amplitudes to obtain <I>S</I>-<I>N</I> curves were bigger than 0.2% proof stress for both types of fatigue tests and it was recognized that specimens hardened during the fatigue tests. Ligaments were observed on the fracture surface between the fish-eye and the specimen surface. In the relationship between the width of the ligament and the plastic zone size at tip of the fish-eye estimated by using cyclic 0.2% proof stress as yield strength, there is no good correlation between them on the whole. But the data plots could be classified into three types, that is, one where good correlation was recognized between the two and the others where the plastic zone sizes were estimated bigger or smaller comparing with the width of the ligament. A range of histogram of hardness measured at a depth of 40<I>μ</I>m from the specimen surface at the cross section of a fatigued specimen expanded to higher levels of hardness than that at a depth of 150<I>μ</I>m. The hardened region at the surface layer of the fatigued specimen was considered to be a crystal grain where slip deformation occurs easily depending on the relationship between crystallographic orientations and loading axis, and hardening due to dynamic strain aging occurs effectively. Crystal grains at the specimen surface where fatigue crack should form basically hardened during the fatigue test, and then, it became difficult for fatigue crack to initiate from the grains. During this period fatigue crack initiated at an internal defect such as a nonmetallic inclusion and internal fracture with the fish-eye occurred.
- 日本材料学会の論文
著者
関連論文
- 低合金鋼の高温疲労におけるフィッシュアイを伴う内部破壊と動的ひずみ時効による表面改質
- 613 SUP12鋼ショットピーニング材における疲労内部破壊の起点(表面処理II,疲労破壊の防止と評価,オーガナイスドセッション1)
- 418 フェライト系ステンレス鋼 SUS430 における弾性係数のヒート間変動と超音波伝ぱ特性の特異性
- 238 細胞骨格の発達方向性がせん断接着力・剥離エネルギーに及ぼす影響(OS1-13 : 生体マイクロ・ナノ新技術(2),マイクロ・ナノバイオメカニクス)
- 425 材料-細胞間接着における接着斑・細胞骨格がせん断接着力に及ぼす影響
- 金属疲労はどのようにして起こるのか(はじめての精密工学)
- JISばね鋼鋼材の弾性係数
- 332 JIS ばね鋼鋼材の弾性係数
- 工具鋼の高サイクル疲労強度に及ぼす介在物, 炭化物の影響(疲労)
- 高強度鋼の疲労強度と疲労き裂発生・進展
- 低合金鋼の高温における超高サイクル域の疲労破壊
- 化学成分と熱処理による機械構造用鋼の弾性係数の変化
- 316 SUP12鋼ショットピーニング材の疲労における内部破壊の様相(疲労特性に及ぼす組織・表面状態の影響II,疲労における機構と評価,オーガナイスドセッション1)
- 308 低合金鋼の高温疲労における内部破壊機構(疲労に及ぼす環境の影響II,疲労における機構と評価,オーガナイスドセッション1)
- 503 高強度鋼の長寿命域における疲労破壊機構(GS-3 疲労(1))
- 102 高温における金属材料の長寿命疲労特性について
- 残留応力分布下で形成されるフィッシュアイ形状の有限要素法による解析
- ステンレス鋼SUS316NGの300°Cにおける疲労破壊に対する予加工と動的ひずみ時効の効果
- ショットピーニング処理されたばね鋼における疲労内部破壊に及ぼす不完全焼入れ組織の影響
- 低合金鋼の高温高サイクル疲労におけるフィッシュアイ破壊
- ショットピーニング処理されたばね鋼ＳＵＰ１２相当材に形成される疲労フィッシュアイの形態
- ステンレス鋼ＳＵＳ３１６ＮＧの３００℃における高サイクル疲労強度に及ぼす切欠き効果の特異性
- Stepwise S-N Curve and Internal Fracture of Austenitic Stainless Steel under High Temperature and High Cycle Fatigue Conditions