Preparation of vanadium-phosphorus mixed oxide (P/V=1) catalysts and their application to oxidation of butane to maleic anhydride.
スポンサーリンク
概要
- 論文の詳細を見る
Several vanadium–phosphorus mixed oxides with a P/V ratio=1 have been prepared and the relationships between the structure of catalyst and the catalytic function for the selective oxidation of butane to maleic anhydride were examined. As revealed from XRD, IR, XPS, and redox titration studies, five among them were presumably composed of crystalline single phases, that is, α-VOPO<SUB>4</SUB>, β-VOPO<SUB>4</SUB>, and (VO)<SUB>2</SUB>P<SUB>2</SUB>O<SUB>7</SUB> as well as unknown phases X<SUB>1</SUB> and X<SUB>2</SUB>. The valences of the vanadium of these catalysts were close to five, except for (VO)<SUB>2</SUB>P<SUB>2</SUB>O<SUB>7</SUB> (the valence was four). These phases were prepared, respectively, by controlling the kind of precursors and the calcination conditions. The selectivity to maleic anhydride differed markedly among these catalysts, although the rate did not change much when it was normalized to surface area. The selectivity at 440 °C was less than 20% for α- and β-VOPO<SUB>4</SUB>, 40% for X<SUB>1</SUB> and X<SUB>2</SUB>, and 70% for (VO)<SUB>2</SUB>P<SUB>2</SUB>O<SUB>7</SUB>. Amorphous phases having V<SUP>4+</SUP> were much less selective than (VO)<SUB>2</SUB>P<SUB>2</SUB>O<SUB>7</SUB>. No structural changes of the catalysts after use were observed in the cases of α-, β-VOPO<SUB>4</SUB>, and (VO)<SUB>2</SUB>P<SUB>2</SUB>O<SUB>7</SUB>. Therefore, the effective phase for selective oxidation of butane to maleic anhydride was speculated to be a phase like (VO)<SUB>2</SUB>P<SUB>2</SUB>O<SUB>7</SUB> in which the valence of vanadium is four and the structure is stable under the reaction conditions.
- 公益社団法人 日本化学会の論文
著者
-
Okuhara Toshio
Department Of Applied Chemistry Faculty Of Engineering The University Of Tokyo
-
Misono Makoto
Department Of Applied Chemistry Faculty Of Engineering The University Of Tokyo
-
Shimoda Tomoaki
Department of Synthetic Chemistry, Faculty of Engineering, The University of Tokyo
関連論文
- Migration of Copper Ions in Cu-MFI without Destruction of Zeolite Lattice or Dealumination upon Hydrothermal Treatment at 923K
- Microporous Heteropoly Compound as a Shape Selective Catalyst : Cs_H_PW_O_
- Selective Alkylation of p-Xylene with 2-Methylpropene by 12-Tungstophosphoric Acid
- Mobility and Exchange of Protons and Methanol Molecules in H_3PW_O_ Pseudoliquid Phase Detected by Solid State NMR
- Active crystal Face of Vanadyl Pyrophosphate for Catalytic Oxidation of n-Butane to Maleic Anhydride
- Alkylation of Isobutane with Butenes Catalyzed by a Cesium Hydrogen Salt of 12-Tungstophosphoric Acid
- Skeletal Isomerization of n-Butane Catalyzed by an Acidic Cesium Salt of 12-Tungstophosphoric Acid
- Novel Microstructures of Self-Assembled Microcrystallites of (NH_4)_3PW_O_ and Cs_3PW_O_
- Porous Aggregates of Unidirectionally Oriented(NH_4)_3PW_O_Microcrystallites : Epitaxial Self-Assembly
- Surface Acidity of Cesium Hydrogen Salts of 12-Tungstophosphoric Acid Characterized by Low-Temperature CO Adsorption
- In Situ Raman Spectroscopic Investigation of Surface Redox Mechanism of Vanadyl Pyrophosphate
- The First Direct Detection of Rapid Migration of Acidic Protons between Heteropolyanions in H_3PW_O_・nH_2O (n
- Protocataltsis of H_3PW_O_-Choloophenol Decomposotion in Aqueous Media^
- Photocatalyzed Decomposition of 4-Chlorophenol by Keggin-Type Heteropolytungstate^#
- Catalytic Removal of Trimethylamine, an Offensive-Odor Component, by Selective Oxidative Decomposition to N_2, Co_2, and H_2O over Copper-Exchanged Zeolites
- Essential Role of Acidity in the Catalytic Reduction of Nitrogen Monoxide by Methane in the Presence of Oxygen over Palladium-Loaded Zeolites
- Oxidation of Cyclohexane with Molecular Oxygen Efficiently Catalyzed by Di-Iron(III)-Substituted Silicotungstate, γ-SiW_{Fe(OH_2)}_2O_^, Including Radical-chain Mechanism
- Remarkable Effect of Iron-Substitution for Molybdenum in Phosphododecamolybdate on Oxidative Dehydrogenation of 2-Propanol
- Hydrothermal Synthesis of Cubic Mesostructured Vanadium-Phosphorus Oxide
- Promotive Effects of the Addition of Alkaline Earth Metals to Ce-ZSM-5 Catalyst for the Reduction of Nitrogen Monoxide in the Presence of Propene and Oxygen
- Comparison of Catalytic Decomposition of Dinitrogen Oxide and Nitrogen Monoxide over Cu/ZSM-5 and Cu/Y Zeolites
- Catalytic Reduction of Nitrogen Monoxide by Methane over Palladium-Loaded Zeolites in the Presence of Oxygen
- Chemical Species Active for Selective Oxygenation of Methane with Hydrogen Peroxide Catalyzed by Vanadium-containing Compounds
- Stereochemical studies of elimination reactions of 2-bromobutane and 2,3-dibromobutane over bivalent-ion exchanged silica gels.
- Stereochemical studies of elimination reactions of 2-bromobutane and 2,3-dibromobutane over alkali-ion exchanged silica gels.
- Effects of alkali metals added to silica-supported ruthenium catalysts on hydrogenation of carbon monoxide.
- Catalysis by heteropoly compounds. XII. Absorption properties of 12-tungstophosphoric acid and its salts.
- Catalysis by heteropoly compounds. XIII. An infrared study of ethanol and diethyl ether in the pseudoliquid phase of 12-tungstophosphoric acid.
- Catalytic properties of perovskite-type mixed oxides (ABO3) consisting of rare earth and 3d transition metals. The roles of the A- and B-site ions.
- Effects of addition of vanadium to alumina-supported ruthenium catalyst on adsorption and hydrogenation of carbon monoxide.
- Novel effects of K-addition to Ru/SiO2 on conversion of cyclohexane.
- Catalysis by heteropoly compounds. III. The structure and properties of 12-heteropolyacids of molybdenum and tungsten (H3PMo12-xWxO40) and their salts pertinent to heterogeneous catalysis.
- Catalytic properties of iron oxide. III. Oxidative dehydrogenation of butenes over iron oxide catalysts.
- The dehydrogenation of cyclohexane by the use of a porous-glass reactor.
- Catalytic properties of iron oxides. II. Isotopic exchange of oxygen, oxidation of carbon monoxide, and reduction-oxidation mechanism.
- Analysis of thermal desorption curves for heterogeneous surfaces. I. A linear variation of the activation energy of desorption.
- Stereospecific Dehydrobromination of dl- and meso-2,3-Dibromobutanes over Solid Catalysts
- The Catalytic Activity and Selectivity of Acidic Metal Salt Catalysts for n-Butene Isomerization
- Catalyst Isotope Effect in n-Butene Isomerization Catalyzed by Metal Sulfates
- Preparation of vanadium-phosphorus mixed oxide (P/V=1) catalysts and their application to oxidation of butane to maleic anhydride.