Temperature programmed desorption study of water adsorbed on metal oxides. I. Anatase and rutile.
スポンサーリンク
概要
- 論文の詳細を見る
The adsorbed state of water on TiO<SUB>2</SUB> was studied by temperature programmed desorption (TPD) in the range 0–1000 °C. Pure anatase and rutile samples, the TPD spectra of water from which were not affected by any contaminant, could be obtained by the hydrolysis of titanium oxalate and tetrachloride solutions, respectively. Two desorption peaks were observed for anatase with the peak maxima at 69–127 (I) and 191–256 °C (II), and three for rutile at 32–90 (I), 188–265 (II), and 310–356 °C (III). The sum of adsorbed amounts for peaks II, and III are within a monolayer coverage, that of peak I exceeding it. The enthalpies of adsorption were evaluated to be 36 and 55–69kJ·mol<SUP>−1</SUP> for peaks I and II of anatase, and 36, 64, and 104 kj·mol<SUP>−1</SUP> for peaks I, II, and III of rutile, respectively. From these results, the corresponding adsorbed species of peak I was tentatively assigned to physical adsorption, that of peak II to chemisorption on surface oxygen ion by hydrogen bond, and that of peak III to chemisortpion on Ti<SUP>4+</SUP> by the coordination of oxygen atom of water molecule. The last species may be dissociated into surface OH groups.
著者
-
Kagawa Shuichi
Department Of Applied Chemistry Faculty Of Engineering
-
EGASHIRA Makoto
Department of Materials Science and Engineering, Faculty of Engineering
-
Seiyama Tetsuro
Department of Materials Science and Technology, Faculty of Engineering, Kyushu University
-
Seiyama Tetsuro
Department of Alaterials Science and Technology, Faculty of Engineering, Kyushu University
-
Kawasumi Shohachi
Department of Materials Science and Engineering, Faculty of Engineering, Nagasaki University
-
Egashira Makoto
Department of Industrial Chemistry, Faculty of Engineering, Nagasaki University
-
Egashira Makoto
Department of Materials Science and Engineering, Faculty of Engineering, Nagasaki University
関連論文
- リンゴ酸添加法で合成したLa0.8Sr0.2MO3(M=Co,Mn)ペロブスカイトの過酸化水素イオン分解活性に対する表面積の影響
- Identification of Active Crystalline Phase in La-K-Cu-V Mixed Oxide for the Simultaneous Removal of Nitrogen Oxides and Diesel Soot
- Catalytic Activity of Perovskite-type La_Sr_M_Cu_yO_3 (M=Al, Mn, Fe, Co) for CO Oxidation and NO-CO Reactions. Influence of the Simultaneous Substitution of Cu and Ru
- Simultaneous Catalytic Removal of Nitrogen Oxides and Soot by Copper-Loaded MFI Zeolites
- Synthesis of Manganite Perovskites by Reverse Homogeneous Precipitation Method in the Presence of Alkylammonium Cations
- Micelle-Templated Mesophases of Phenol-Formaldehyde Polymer
- Effect of Transition Metal Additives on Catalytic Activity of SnO_2 for the Selective Reduction of NO with C_2H_4
- Control of Size of CdS Formed in Organized Molecular Assembly Films by Molecular Structure and Film Orderliness
- Third Harmonic Generation from Quantum-State PbS Embedded in Langmuir-Blodgett Film Matrix
- Novel Multibilayer Film Incorporating Electro- and Photo-Chemically Active Decatungstate Anion
- Selective Reduction of Nitrogen Monoxide with Hydrocarbons over SnO_2 Catalyst
- Sicセラミックスから発生するマイクロ波誘起常圧Arによる毒性ハロゲン化炭化水素の分解
- 大気圧下でSiCセラミックスから発生するマイクロ波誘起Arプラズマによるトリクロロエチレンの分解
- 貴金属を担持したIn2O3系センサのトリメチルアミンガス感度に及ぼす膜厚の影響
- Inhibition of NO Decomposition Activity of Perovskite-type Oxides by Coexisting Carbon Dioxide
- Effect of Oxide Composition of Spinel-type Copper Chromites on the Catalytic Activity for the Simultaneous Removal of NOx and Soot Particulate
- Temperature programmed desorption study of water adsorbed on metal oxides. I. Anatase and rutile.
- Mechanism of the reduction of nitric oxide with ammonia over Cu(II) ion-exchanged zeolites.
- Oxyhydrative scission of trans-2-butene in the liquid phase under pressure.
- Enhancement of catalytic activity of copper ion-exchanged Y type zeolites for the decomposition of nitrogn monoxide.
- The Catalytic Dehydrohalogenation of Haloethanes on Solid Acids and Bases
- Elimination Reactions of Ethylene Halohydrins on Solid Catalysts
- Structure of the Vanadium-Potassium Catalyst during the Oxidation of Sulfur Dioxide and the Oxidation Mechanism
- Oxidation of ketones over metal oxide catalysts. II. Biacetyl synthesis over Co3O4-lanthanoid oxide catalysts.
- The Thermal Decomposition and Reduction of Silver(I) Oxide
- Hydration of Propene over Proton- and Metal Ion-Exchanged Zeolite Catalysts at Atmospheric Pressure.
- Elimination Reactions of Propylene Chlorohydrins over Solid Acids
- The Dehalogenation of Haloalkanes on SiO2-supported Metals