種々の界面におけるポリ(メタクリル酸メチル)の分子鎖熱運動性
スポンサーリンク
概要
- 論文の詳細を見る
Thermal molecular motion of poly(methyl methacrylate) (PMMA) at various interfaces, gases and liquids, was discussed. The α<font size="-1">a</font>- and β-relaxation processes were clearly observed even at the air interface. Both relaxation temperatures at the air interface were lower than the corresponding ones in the bulk. In addition, the extent to which the peak temperature for the surface relaxation processes fell below that of the bulk strongly depended on the stereoregularity of the films. Then, thermal molecular motion of PMMA was analyzed at gaseous carbon dioxide (CO<font size="-1">2</font>) interface. It was more enhanced than that at gaseous nitrogen interface because CO<font size="-1">2</font> molecules were sorbed in the interfacial region, which played as plasticizing agents. Finally, mechanical properties of PMMA were also studied at interfaces with liquids such as water, hexane and methanol. The modulus decreased closer to the outermost region of the film. The extent to which the modulus decreased in the interfacial region was consistent with the amount of liquid sorbed into the film. Therefore, it can be claimed that interfacial molecular motion of polymers can be regulated on the basis of the aggregation states.
著者
-
藤井 義久
九州大学大学院工学研究院
-
Tanaka K
Agroscience Research Laboratories Sankyo Co. Ltd.
-
田中 敬二
九州大学大学院 統合新領域学府 オートモーティブサイエンス専攻
関連論文
- ポリブチレンテレフタレートの接着挙動におよぼす熱処理条件の影響(有機材料・薄膜・界面・デバイス/フィルムベースデバイスのための界面制御とプロセス技術)
- ナフィオン膜の電解条件下での安定性に及ぼす圧力の影響
- 高分子超薄膜の界面物性評価とデバイス応用(有機材料・薄膜・界面・デバイス/フィルムベースデバイスのための界面制御とプロセス技術)
- 水と接触した高分子の物性測定と機能発現への展開
- 高分子間ナノ接着における発現機構の解明
- 臨界絡み合い分子量を超える長さを有する環状ポリスチレンの積層膜界面における相互拡散
- 走査粘弾性顕微鏡の力学モデル化と高分子表面への応用
- 表面, 界面および膜特集号に添えて
- ポリマーブレンドにおける表面・界面の濃縮現象
- Chain Conformation Effects on Molecular Motions at the Surface of Poly(methyl methacrylate) Films