Mill blends of various styrene-butadiene random copolymer rubbers on today′s market (styrene content: 23.5-46wt%) and styrene-butadiene-styrene block copolymer (styrene content: ca. 25wt%) were studied. Hardness and compression modulus of uncured blends were measured and the shapes of curves of blend ratio dependence of physical properties and the state of dispersion polymers were paid attention to.And it was found that this blend system is clearly a microheterogeneous blend system but that the zone sizes of dispersed polymers are small and the curves of hardness and compression modulus (in logarithm) against blend ratio are almost linear. And it was also found that the softening phenomenon after remilling (the roll surface temperature: 60°C) is hardly observed.And further consideration leads us to presume a strong mutual interaction between polymers to be responsible for this phenomenon.
- 日本ゴム協会の論文
著者
関連論文
- 食品用ラップ
- トレッドとしてのSBR/EPDMおよびSBR/BR/EPDMブレンド物について
- トレッドポリマーとしての1, 4-ヘキサジエン-EPDMとエチリデンノルボルネン-EPDMの差について : EPDMタイヤに関する研究 (第4報)
- トレッドポリマーとしてのEPDMについて
- オールEPDMタイヤの試作
- 低シス・ポリブタジエンゴムと高シス・ポリブタジエンゴムのブレンド
- 高シス・ポリブタジエンゴムとスチレン・ブタジエン・スチレン・ブロック共重合体のブレンド
- スチレン・ブタジエン共重合体ゴム〜一般用スチロール樹脂ロールブレンド物の熱処理による混合状態の変化
- ステレン・ブタジエン共重合体ゴム〜一般用スチロール樹脂ブレンド物のロール再練りによる軟化現象
- スチレン・ブタジエン・スチレンブロック共重合体〜一般用スチロール樹脂ブレンドの転相領域に関する考察
- スチレン・ブタジエン・スチレン・ブロック共重合体と一般用スチロール樹脂のブレンド
- ポリブタジエンゴムとスチレン・ブタジエン・スチレン・ブロック共重合体のブレンド
- ポリブタジエンゴム-一般スチロール樹脂ブレンド物のロール再練りによる軟化現象に関する研究
- ポリブタジエンゴム-スチロール樹脂ブレンド物の一般物性に関する研究
- ポリブタジエンゴム-一般用スチロール樹脂ブレンド加硫物の物性に及ぼす混合状態の影響
- 低シスポリブタジエンの配合物に及ぼすプロセスオイルの影響-1- (ステレオラバーの諸問題(特集))
- ポリブタジエンをブレンドしたゴムの粘弾性
- エチレン・プロピレンゴムとスチレン・ブタジェン・スチレン・ブロック共重合体のブレンド
- BRの粘着性 (接着と粘着(特集))
- ランダム・スチレン・ブタジェン共重合体ゴムとスチレン・ブタジェン・スチレン・ブロック共重合体のブレンド
- 射出成形機による加硫 (ゴムの高温高速加硫(特集))
- ミクロ構造の異なるBR同志のブレンド (ポリマーブレンドの諸問題(特集)) -- (ポリマーのブレンディング-1,2-)