Viscoelasticities of polybutadiene (PB), NR, SBR and their blends (50/50) were measured by VIBRON-II manufactured by Toyo Measuring Instrument. Dilatometry was also applied for the investigation of their crystallinities.<BR>The following results were obtained.<BR>(1) Crystallinity is observed with cured high cis PB, but the temperature of crystallinity is low as compared with that of raw polymer. Difference of Cis-content results in the difference of the temperature of crystallinity. In the case of low cis PB, crystallinity is never observed in both raw and cured polymers.<BR>(2) Blending of NR with either of PB produces a heterogeneous mixture, but low cis PB excels high cis PB in the compatibility. In the case of high cis PB, crystallinity is observed even in the blending with NR.<BR>(3) Blending of SBR with each of PB produces a homogeneous mixture except for one of high cis PB and crystallinity is almost never observed in the case of high cis PB.
著者
関連論文
- トレッドとしてのSBR/EPDMおよびSBR/BR/EPDMブレンド物について
- トレッドポリマーとしての1, 4-ヘキサジエン-EPDMとエチリデンノルボルネン-EPDMの差について : EPDMタイヤに関する研究 (第4報)
- トレッドポリマーとしてのEPDMについて
- オールEPDMタイヤの試作
- 低シス・ポリブタジエンゴムと高シス・ポリブタジエンゴムのブレンド
- 高シス・ポリブタジエンゴムとスチレン・ブタジエン・スチレン・ブロック共重合体のブレンド
- スチレン・ブタジエン共重合体ゴム〜一般用スチロール樹脂ロールブレンド物の熱処理による混合状態の変化
- ステレン・ブタジエン共重合体ゴム〜一般用スチロール樹脂ブレンド物のロール再練りによる軟化現象
- スチレン・ブタジエン・スチレンブロック共重合体〜一般用スチロール樹脂ブレンドの転相領域に関する考察
- スチレン・ブタジエン・スチレン・ブロック共重合体と一般用スチロール樹脂のブレンド
- ポリブタジエンゴムとスチレン・ブタジエン・スチレン・ブロック共重合体のブレンド
- ポリブタジエンゴム-一般スチロール樹脂ブレンド物のロール再練りによる軟化現象に関する研究
- ポリブタジエンゴム-スチロール樹脂ブレンド物の一般物性に関する研究
- ポリブタジエンゴム-一般用スチロール樹脂ブレンド加硫物の物性に及ぼす混合状態の影響
- 低シスポリブタジエンの配合物に及ぼすプロセスオイルの影響-1- (ステレオラバーの諸問題(特集))
- ポリブタジエンをブレンドしたゴムの粘弾性
- エチレン・プロピレンゴムとスチレン・ブタジェン・スチレン・ブロック共重合体のブレンド
- BRの粘着性 (接着と粘着(特集))
- ランダム・スチレン・ブタジェン共重合体ゴムとスチレン・ブタジェン・スチレン・ブロック共重合体のブレンド
- 射出成形機による加硫 (ゴムの高温高速加硫(特集))