ポリブタジエンゴム-一般スチロール樹脂ブレンド物のロール再練りによる軟化現象に関する研究
スポンサーリンク
概要
- 論文の詳細を見る
Forty wt % blend of general purpose polystyrene resin with polybutadiene rubber is very hard and shows poor processability, when it is prepared by open mill under ordinary conditions.<BR>However, this hard compound was found to be softened and show excellent processability when it is remilled by open mill at a surface temperature of 90°C.<BR>The effects of blend ratio and remilling temperature were studied with the following results obtained. The softening is observed clearly when the blend is composed of 20 to 60 wt % of general purpose polystyrene resin and the surface temperature of remilling roll is below 120 °C. This phenomenon is caused by socalled phase transition of general purpose polystyrene resin from continuous phase to non-continuous one.
著者
関連論文
- トレッドとしてのSBR/EPDMおよびSBR/BR/EPDMブレンド物について
- トレッドポリマーとしての1, 4-ヘキサジエン-EPDMとエチリデンノルボルネン-EPDMの差について : EPDMタイヤに関する研究 (第4報)
- トレッドポリマーとしてのEPDMについて
- オールEPDMタイヤの試作
- 低シス・ポリブタジエンゴムと高シス・ポリブタジエンゴムのブレンド
- 高シス・ポリブタジエンゴムとスチレン・ブタジエン・スチレン・ブロック共重合体のブレンド
- スチレン・ブタジエン共重合体ゴム〜一般用スチロール樹脂ロールブレンド物の熱処理による混合状態の変化
- ステレン・ブタジエン共重合体ゴム〜一般用スチロール樹脂ブレンド物のロール再練りによる軟化現象
- スチレン・ブタジエン・スチレンブロック共重合体〜一般用スチロール樹脂ブレンドの転相領域に関する考察
- スチレン・ブタジエン・スチレン・ブロック共重合体と一般用スチロール樹脂のブレンド
- ポリブタジエンゴムとスチレン・ブタジエン・スチレン・ブロック共重合体のブレンド
- ポリブタジエンゴム-一般スチロール樹脂ブレンド物のロール再練りによる軟化現象に関する研究
- ポリブタジエンゴム-スチロール樹脂ブレンド物の一般物性に関する研究
- ポリブタジエンゴム-一般用スチロール樹脂ブレンド加硫物の物性に及ぼす混合状態の影響
- 低シスポリブタジエンの配合物に及ぼすプロセスオイルの影響-1- (ステレオラバーの諸問題(特集))
- ポリブタジエンをブレンドしたゴムの粘弾性
- エチレン・プロピレンゴムとスチレン・ブタジェン・スチレン・ブロック共重合体のブレンド
- BRの粘着性 (接着と粘着(特集))
- ランダム・スチレン・ブタジェン共重合体ゴムとスチレン・ブタジェン・スチレン・ブロック共重合体のブレンド
- 射出成形機による加硫 (ゴムの高温高速加硫(特集))