窒素イオン注入した浸炭焼入鋼及び調質鋼のすべり摩耗特性
スポンサーリンク
概要
- 論文の詳細を見る
As specific applications of ion implantation to surface modification, nitrogen ion implantation was applied to S45C, a steel widely used for machine structural applications, to SCM 440 thermally refined steel, and to SCM 415 carburized steel, and their friction and wear characteristics were examined. The results can be summarized as follows1) In an effort to improve the seizure resistance of SCM 415 carburized steel, investigation centered on a certaining the friction behavior of the nitrogen-ion-implanted surface layers using a Favill Le Vally friction testing machine. It was found that under unlubricated sliding friction, the effect of carburizing treatment in the preceding step was great. Under lubricated sliding friction, however, the load vs. friction coeffient curve for SCM 415 with nitrogen ion implantation was similar to that without, the load at which seizure started was 2000kgf or more, and higher loads could be withstood if ion fluences were increased.2) The wear volume of the steels subjected and not subjected to nitrogen ion implantation in 1) above was measured to determine their wear characteristics. Since the modified layer of the implanted steels was thinner than that of the gas-nitrocarburized steel, they tended to suffer greated wear at short friction distances. When a modified layer existed, however no great difference in wear resistance was observed between the two kinds of steel.3) Using a pin-ring-type wear testing machine, a series of lubricated sliding wear tests were carried out on thermally refined steel and thermally refined nitrogen-ion-implanted steel under conditions under which adhesion and thermal wear occur. It was observed that the nitrogen-ion implanted steel had a lower specific wear volume than the thermally refined steel.4) Analysis of the nitrogen-ion-implanted surface layers and observation of the friction surfaces suggest that the improvement in seizure resistance and wear resistance with nitrogen ion implantation is attributable to the formation of iron nitride ε-Fe2-3N or higher iron nitride ζ-Fe2N due to the concentration of nitrogen ions in the surface layer, and that these iron nitrides have a substantial lubricating effect.
- 社団法人 表面技術協会の論文
著者
関連論文
- マグネシウムダイカストAZ91Dの化成処理および陽極酸化により生成した皮膚の組成と形態
- H_2-H_2O-Ar混合ガス中で酸化したFe-1.26および2.12mass%Al合金の組織変化と内部酸化
- アルミニウム急冷合金陽極酸化皮膜の静電容量特性と皮膜構造
- イオンビーム励起によるCeイオン注入α-AI_2O_3の発光特性
- マグネシウムダイカストAZ91Dの陽極酸化により生成した皮膜の構造と成長機構
- マグネシウムダイカストAZ91Dの化成処理により成長した表面皮膜の構造と生成機構
- 電気化学的インピーダンス法によるSargent浴中のクロム電析機構の解析
- ガラス状炭素へイオン注入したNaの深さ分布と注入層の密度変化
- 窒素イオン注入した浸炭焼入鋼及び調質鋼のすべり摩耗特性
- 窒素イオン注入により生成するTi窒化物とZr窒化物のXPSによる解析
- IVa族遷移金属への窒素イオン注入による表層薄膜組成と着色性
- 明治・大正・昭和前期刊行 表面処理関係図書目録
- 日本表面技術分野における独自技術の開発を : 第111回講演大会を迎えるにあたって
- 石田 春律の「金屋子縁記抄」とその周辺
- 近世の古鉄流通と再生-古鉄商に見る鉄のリサイクル-
- 近世初期の日蘭貿易による鉄輸出の実態
- 表面処理用語の語源散策 「錆」と「腐食」の語史
- 「カネ」から「金属」へ -Metalの訳語について-
- 「表面」の語史
- 表面処理用語の語源散策(その6) -メタリコンから溶射へ-
- 表面処理用語の語源散策 -ぶりきの履歴書-
- 史料でたどる日本の前近代めっきの歴史(その2) -金めっきから電気めっき技術の移植まで-
- 幕末・明治期刊行図書にみる電気めっき受容の一断面
- 金属窒化物層の組成及び耐食性
- 制御雰囲気のもとでの加熱処理によるステンレス鋼の不動態化
- クロム板へのMeV窒素イオン多重注入 : II. 窒素濃度プロファイルに対する熱処理効果
- クロム板へのMeV窒素イオン多重注入 : I. 改質層の結晶性に対する注入基板温度の影響
- 金属バナジウムへの窒素イオン注入により生成する表面窒化薄層の特性
- 4a及び5a族遷移金属の水素吸収に及ぼす窒素イオン注入の影響 (イオンビ-ムによる表面改質とパッシベ-ション)
- 金属クロムにイオン注入された窒素の深さ分布に及ぼす熱処理の影響
- マグネシウム--その誕生とおいたち (マグネシウムの表面処理)
- Nitrogen distribution of ion implanted into electrodeposited chromium films.