アルミナセラミックスの曲げ疲労
スポンサーリンク
概要
- 論文の詳細を見る
In order to make clear the effect of repetition of loading on Al2O3 ceramics, bending fatigue experiments were carried out under pulsation or reversion of loading with the frequencies of 10Hz, 25Hz and 50Hz, and under static loading in dry atmosphere at 288K. The results are summerized as follows;(1) Frequency dependence of fatigue life was evidently seen in the case of repetition. Time to fracture was shorter for high frequency.(2) The fatigue life under reversion of bending was considerably shorter than the fatigue life under the pulsation of bending.(3) For the same maximum stress level, time to fracture under a pulsation of loading was shorter than that of static loading. At the frequency of 50Hz, the fatigue life was about one tenth of the static case.
- 社団法人 日本材料学会の論文
著者
関連論文
- 1362 膝蓋骨-膝蓋腱-脛骨結節複合体の動的挙動
- 鋼の衝撃疲労と通常疲労の比較研究
- PMMA丸棒内のねじり波の減衰
- 粘弾性丸棒内のねじり波の伝ぱ
- 有限長棒の衝撃応力
- 衝撃力によるアルミニウム合金のき裂成長開始
- 衝撃力による鋼材内のき裂成長開始 : 静的予荷重および温度の影響
- 衝撃力による鋼材内のき裂成長開始
- ショットピーニング材の疲労寿命に及ぼす複数表面き裂の分布特性の影響
- 繰返しに伴うき裂長さ分布の変化を考慮した腐食疲労寿命推定
- 低エネルギの繰返し衝撃によるCFRP積層材の損傷
- 粒子の斜め衝撃によるセラミックスの損傷
- 粒子の繰返し衝撃による炭化けい素の損傷
- 323 粒子の斜め衝撃による炭化珪素セラミックスの損傷(材料の耐摩耗性・***ージョン特性)
- 圧縮荷重を受けるスリット近傍の弾塑性応力解析
- 高マンガン鋼の疲労強度特性に及ぼす介在物の影響
- 板弁の衝撃疲労寿命の改善
- 対称積層構造材の振動特性解析法の研究 : CFRP円筒シェルの加振実験
- 焼入れ焼戻し鋼の衝撃圧縮による塑性域発生
- 衝撃圧縮による鋼の塑性域発生 : 第2報,2個の試験片に対する接触面と試験片長さの影響
- 衝撃圧縮による鋼の塑性域発生
- 衝撃破壊靱性の特性
- 多能衝撃試験機の開発と衝撃強度の新表示法
- 強度設計と時間 (とき)
- 八点鐘 (とき)
- 炭素鋼予ひずみ材の腐食疲労寿命とき裂進展
- 円形RC橋脚の耐震補強に関する実験的な研究
- アルミナセラミックスの熱衝撃疲労
- アルミナセラミックスの曲げ疲労
- アルミナジルコニアセラミックスの曲げ疲労(疲労特集)
- セラミックスの熱衝撃疲労における裂進展挙動
- 212 セラミックスの熱衝撃疲労におけるき裂進展挙動(セラミックスの強度と疲労)
- アルミナセラミックスの曲げ疲労
- 高軸力を受けるRC柱の炭素繊維シートによる耐震補強実験
- 繰返し熱衝撃を受けたセラミックスの残留強度のばらつき
- 129 セラミックスの熱衝撃疲労における微視き裂進展挙動(高温き裂と損傷力学)
- 119 氷の破壊じん性 : き裂先端形状の影響(破壊靱性および高温強度)
- 膝蓋骨-膝蓋腱-脛骨結節複合体の衝撃応答解析 : 第2報
- 膝蓋骨-膝蓋腱-脛骨結節複合体の衝撃応答解析
- 溶接線に近いき裂の衝撃力による成長
- 1080 円形RC橋脚の耐震補強に関する実験的な研究(補修・補強(材料・構造))
- 2035 高軸力を受けるRC柱の炭素繊維シートによる耐震補強実験(コンクリート構造の耐震補強・技術 既存構造物の耐震補強)