粗大結晶軟鋼の引張りにおける結晶状態の変化 : 擬コッセル線による結晶体の観察(第2報)
スポンサーリンク
概要
- 論文の詳細を見る
The behaviour of the individual grain and that of the inside grain of the specimen deformed by tension were investigated by the back reflection divergent X-ray beam method, to confirm their correlation with the behaviour of the specimen as a whole.<BR>Coarse-grained polycrystalline plate specimens of low carbon steel were prepared by the strainannealing method. The grain sizes of the specimens were about 1.7, 7 and 5mm for sample A, B and C respectively.<BR>The horizontal type capillary X-ray tube apparatus (Rigaku Denki make) was used to obtain Fe-Kα radiation.<BR>First, to examine the structural change of crystals, pseudo-Kossel patterns were taken with the samples A and B at several stages of strain after the load were removed. Stresses and strains of specimens were also measured simultaneously to provide the nominal stress-strain diagram.<BR>Then, the relative lattice rotation was examined in an unstrained and strained state at two different positions in a grain with sample C.<BR>It was observed that the pseudo-Kossel patterns became irregular with deformation, showing local line broadening, kinking and shifting, when the specimens were stretched over the proportional limit, and that the diffraction lines broadened as a whole in the state of greater deformation.<BR>In the range between the proportional limit and the stress level at which linear hardening in the load-elongation diagram started, the kinking, shifting and broadening of the diffraction lines increased.<BR>When the specimen was deformed by tension, the relative lattice rotation was observed at two different positions in a grain, in the early stage of plastic deformation.<BR>In the stress range corresponding to the linear hardening, most diffraction lines of the obtained pseudo-Kossel patterns showed kinking, shifting and broadening, irrespective of the kinds of latticeplane.<BR>It was seen from these results that in the load-elongation diagram, the curved range between the proportional limit and the stress level at which linear hardening started was caused by the fact that the load elastically supported by individual grain or different part of a grain was different from each other.
- 社団法人 日本材料学会の論文
著者
関連論文
- 平行ビーム法におけるX線測定条件が回折線プロフィルに与える影響
- (3-41) ショットピーニングを施したばね鋼平板の静曲げ過程における表面層の降伏について
- 表面層に急激な応力こう配をもつ試料のX線応力測定
- 高周波焼入れした中炭素鋼のX線による残留応力測定
- 入射X線揺銅法による応力測定
- ショットピーニングを施した鋼のX線による応力測定 : X線測定応力と公称応力の対応
- 多重露光写真法によるX線応力測定
- X線回折写真法カメラ用スリットに関する検討
- 新形X線応力測定装置とそれによる測定結果について
- X線応力測定による鋳鉄の疲労強度評価
- 擬コッセル線による結晶方位の決定法
- 平面曲げ荷重によるばね綱の変形と疲労破壊のX線による研究
- 粗大結晶軟鋼の引張りにおける結晶状態の変化 : 擬コッセル線による結晶体の観察(第2報)
- 片状黒鉛鋳鉄および黒心可鍛鋳鉄のX線応力測定
- 両振平面曲げ疲労過程における構造用鋼板の残留応力ならびに半価幅の変化について