ベリロンIIによる銅および亜鉛合金中のベリリウムの吸光光度定量
スポンサーリンク
概要
- 論文の詳細を見る
The sample was dissolved in hydrochloric acid and nitric acid. An aliquot containing 110 μg Be was taken, and pH was with sodium hydroxide solution. Four milliliters of 0.1% Beryllon II solution and 2 m<I>l</I> of 1 <I>N</I> sodium hydroxide solution were added, and the solution was diluted to 25 m<I>l</I> with water. The absorbance at 620 mμ was measured, and the amount of Be was determined referring to a calibration curve. Aluminum as much as 100 times Be did not interfere. The interference from Ca and Mg was removed by masking them with EDTA, and that from Cu and Zn by potassium cyanide. Beryllium in copper and zinc base alloys, in the range from 2.00 to 0.01%, was determined directly without removing copper and zinc.
- 社団法人 日本分析化学会の論文
著者
関連論文
- 2-ヒドロキシ-4-メチルベンズアルデヒド-セミカルバゾンによるガリウムの蛍光定量 : アルミニウム地金への適用
- 2-ヒドロキシ-1-ナフトアルデヒド-セミカルバゾンによるスカンジウムの蛍光定量 : 鉱物試料への適用(無機材料分析のためのスペクトロメトリー)
- 2-ヒドロキシ-5-スルホアニリン-N-サリチリデンによる高純度アルミニウム中の微量ガリウムの蛍光定量
- 2-ヒドロキシベンズアルデヒド-チオセミカルバゾンによるインジウムの蛍光定量
- 2-ヒドロキシ-5-スルホアニリン-N-サリチリデンによる銅及び銅-ベリリウム合金中のベリリウムのけい光定量
- 2,4-ジヒドロキシベンズアルデヒド-セミカルバゾンによる鉄鋼中のアルミニウムのけい光定量
- チオテノイルトリフルオロアセトンとo-フェナントロリンを用いるスズ地金中のカドミウムの溶媒抽出-原子吸光分析
- チオテノイルトリフルオロアセトンを用いる銅の溶媒抽出-原子吸光分析
- 2-ヒドロキシ-5-スルホアニリン-N-サリチリデンとゼフィラミンによる鉄(III)の吸光光度定量
- チオテノイルトリフルオロアセトンとo-フェナントロリンを用いるマンガンの溶媒抽出-原子吸光分析
- チオテノイルトリフルオロアセトンと0-フュナントロリンを用いる亜鉛の溶媒抽出-原子吸光分析
- メチルキシレノールブルーによるビスマスの比色定量
- 粗銅中の銀の吸光光度定量法
- ベリロンIIによる銅および亜鉛合金中のベリリウムの吸光光度定量
- 微量イオウイオンの吸光光度定量法