凍結乾燥法による多孔質セラミック粒子の製造
スポンサーリンク
概要
- 論文の詳細を見る
Porous alumina and magnesia particles were prepared by freeze-dry processing. Freeze dried particles from an aqueous metal salt solution have many pores formed by ice sublimation traces. The particles were calcined to form oxide particles, which still had a porous configuration. When the porous calcined particles were committed to a furnace they became porous ceramic particles. Various factors such as feed concentration of a metal solution, freezing temperature, firing temperature and hold time were investigated to determine how they affect the pore configuration of the particles. The relationships between compressive strength and porosity and between specific surface area and porosity were clarified.
- 社団法人 化学工学会の論文
著者
関連論文
- 数式解照合を柔軟に行うLISPによるCAIシステム
- トリス(2,2'-ビピリジン)ルテニウム(II)-メチルビオローゲン系可視光触媒を用いる水からの長時間水素生成反応
- 多層構造ルテニウム錯体系膜の可視光増感作用を用いる水の光分解
- 凍結乾燥法による耐熱性多孔質セラミックスの製造 (特集 機能性新素材の先端技術)
- 気・固・液分散系を含む二重円筒型光反応器内の光強度分布の推算
- 高気孔率多孔質セラミックスの製造法
- エチレンジアミン-N, N'-ビス[2-(2-ヒドロキシフェニル)アセタト]カドミウム(II)酸イオンとエチレンジアミンテトラアセタト鉄(III)酸イオンとの間の配位子置換反応の反応速度論による機構解析
- 高配向性多孔質セラミックスの製造 (特集 機能性材料製造技術の展望)
- 金属アルコキシド法を用いてSiO_2粒子上に担持したTiO_2の光触媒活性
- 均相系内部照射型光反応器の設計 (化学工学と光利用技術)
- 凍結乾燥法による多孔質セラミックス粒子の製造
- 各種金属塩水溶液の凍結乾燥における乾燥特性
- 濡壁塔を用いた凍結乾燥における凍結粒子の連続製造法 (化工新技術開発トピックス)
- 凍結乾燥における凍結粒子の濡れ壁塔を用いた連続製造法
- 凍結乾燥法によるセラミックス用粉体製造における凍結時の組成偏析について
- 凍結乾燥法における難乾燥性試料へのアンモニア水添加の影響
- 凍結乾燥法によるセラミックス用原料粉体の製造
- 拡散反射板をもった二重円筒型光化学反応器の光吸収
- 内部照射型光化学反応器の光吸収速度--鏡面反応器における反射の影響
- 気泡塔型光化学反応器の光吸収速度について
- 気泡塔型光化学反応器によるトルエンの光塩素化反応について
- 各種金属塩水溶液の凍結乾燥における乾燥特性
- 凍結乾燥法による多孔質セラミック粒子の製造
- 凍結乾燥における凍結粒子の濡れ壁塔を用いた連続製造法
- 凍結乾燥法における難乾燥性試料へのアンモア水添加の影響
- 凍結乾燥法によるセラミックス用粉体製造における凍結時の組成偏析について
- 気泡塔型光化学反応器によるトルエンの光塩素化反応について
- 気泡塔型光化学反応器の光吸収速度について
- 内部照射型光化学反応器の光吸収速度 : 鏡面反応器における反射の影響