鉄粉の抵抗焼結過程の解析
スポンサーリンク
概要
- 論文の詳細を見る
The sintering process of iron powder during flash resistance-sintering was analyzed on the basis of temperature and electric-resistance changes of the compacts. The temperature change for very short time was estimated from the power input value at every moment. The estimated temperature was compared to the compact surface temperature measured by an infrascope, and it was confirmed that the difference between both the temperatures was rather small, and decreased with an increase of set-up current level. From the analysis, it was shown that in the resistance-sintering of metal powder, heat generated at an early stage is mostly due to the contact resistance, between particles, and its fraction decreases as the sintering time proceeds. The rate of decrease depends upon the properties of the metal powder and resistance-sintering conditions.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 焼結による高密度銅圧粉体の膨張現象に関する一考察
- ボールミルによって紛砕したTiH2紛の酸化量の測定
- Cu超微粉の焼結挙動に及ぼすAl2O3粉添加の影響
- 鋳鉄粉の粉末圧延による含黒鉛薄鉄板の作成
- アルミニウム粉の抵抗焼結 : 攪拌摩砕の効果
- アルミナあるいは炭化物粒子添加チタン粉の通電抵抗焼結
- チタン合金粉(Ti-6Al-4VおよびTi-6Al-2Sn-4Zr-6Mo)の通電抵抗焼結
- チタンおよびチタン合金抵抗焼結体の電気抵抗
- 抵抗焼結法によるボロン繊維強化アルミニウムの作製
- 抵抗焼結法によるボロン繊維-チタン複合材の製造
- WC-Co系超硬合金の拡散被覆 : ボロナイジングとシリコナイジングについて
- 鉄鋼科学・技術史委員会教育ワーキング・グループ報告
- 日本鉄鋼工学・技術教育史の連載にあたつて
- 明治初年の開成学校, 工部学校と冶金教育のかかわり : 鉄鋼の歴史のトピックス (3)
- 159 鉄粉の直接熱間圧延の試み(低温靱性, 加工・性質・分析, 日本鉄鋼協会 第 82 回(秋季)講演大会)
- 251 工業用鉄粉の安定性(鋳造・加工・ウィスカー・組織・強度一般, 加工・性質・分析・計測, 日本鉄鋼協会第 80 回(秋季)講演大会講演)
- 鋳鉄粉を利用した高強度焼結材
- 鋳鉄粉・Fe-Si-C系・Ni-C系焼結体の球状黒鉛(2) : 組織と機械的性質
- 鋳鉄粉・Fe-Si-C系・Ni-C系焼結体の球状黒鉛(1) : 黒鉛の性質と球状黒鉛生成の原理
- 金属粉の瞬間抵抗焼結法に関する研究(第2報) : 鉄粉の抵抗焼結について
- 金属粉の瞬間抵抗焼結法に関する研究(第1報) : Ni80-Cr20合金の抵抗焼結について
- 粉末冶金法によって調整したTi-50at%Ni合金の組織
- 鉄粉の抵抗焼結過程の解析
- チタン合金の瞬間抵抗焼結
- 抵抗焼結法による繊維強化金属の製造の試み
- 鋼繊維強化アルミニウムの抵抗焼結
- チタン粉末の抵抗焼結過程の解析
- チタン粉末の瞬間低抗焼結
- 硫酸銅水溶液の加熱による生成物について ぶどう糖による還元析出機構-1-
- チタン紛末の抵抗焼結過程におよぼす焼結条件,粒度,混合粉等の影響