チタン粉末の瞬間低抗焼結
スポンサーリンク
概要
- 論文の詳細を見る
Ti powder (Na reduced, -60 mesh, 0.09 wt% oxygen) was resistance-sintered in air. The dependence of mechanical properties and corrosion resistance' of compacts on the condition of resistance sintering, particle size and history of the powder was studied. The compacts having low oxygen content (0.13%) and excellent mechanical properties (98% theoretical density, tensile strength 40-50 kg/mm<SUP>2</SUP>, elongation 30%) were obtained. The oxygen content in products is affected by the history of the powder rather than by the conditions of resistance sintering. When fresh powder is used, with increasing of power input per unit time and particle size, the oxygen content in the products decreases, resulting in more ductile Ti metal. Corrosion resistance of the resistance-sintered Ti increases with the increase of their apparent density, and their corrosion level is almost the same as that of conventional P/M Ti.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 鋳鉄粉の粉末圧延による含黒鉛薄鉄板の作成
- アルミニウム粉の抵抗焼結 : 攪拌摩砕の効果
- アルミナあるいは炭化物粒子添加チタン粉の通電抵抗焼結
- チタン合金粉(Ti-6Al-4VおよびTi-6Al-2Sn-4Zr-6Mo)の通電抵抗焼結
- チタンおよびチタン合金抵抗焼結体の電気抵抗
- 抵抗焼結法によるボロン繊維強化アルミニウムの作製
- 抵抗焼結法によるボロン繊維-チタン複合材の製造
- 鉄鋼科学・技術史委員会教育ワーキング・グループ報告
- 日本鉄鋼工学・技術教育史の連載にあたつて
- 明治初年の開成学校, 工部学校と冶金教育のかかわり : 鉄鋼の歴史のトピックス (3)
- 159 鉄粉の直接熱間圧延の試み(低温靱性, 加工・性質・分析, 日本鉄鋼協会 第 82 回(秋季)講演大会)
- 251 工業用鉄粉の安定性(鋳造・加工・ウィスカー・組織・強度一般, 加工・性質・分析・計測, 日本鉄鋼協会第 80 回(秋季)講演大会講演)
- 鋳鉄粉を利用した高強度焼結材
- 鋳鉄粉・Fe-Si-C系・Ni-C系焼結体の球状黒鉛(2) : 組織と機械的性質
- 鋳鉄粉・Fe-Si-C系・Ni-C系焼結体の球状黒鉛(1) : 黒鉛の性質と球状黒鉛生成の原理
- 金属粉の瞬間抵抗焼結法に関する研究(第2報) : 鉄粉の抵抗焼結について
- 鉄粉の抵抗焼結過程の解析
- チタン合金の瞬間抵抗焼結
- 抵抗焼結法による繊維強化金属の製造の試み
- 鋼繊維強化アルミニウムの抵抗焼結
- チタン粉末の抵抗焼結過程の解析
- チタン粉末の瞬間低抗焼結
- 硫酸銅水溶液の加熱による生成物について ぶどう糖による還元析出機構-1-
- チタン紛末の抵抗焼結過程におよぼす焼結条件,粒度,混合粉等の影響