噴霧法による多孔質青銅合金粉の製造
スポンサーリンク
概要
- 論文の詳細を見る
In order to improve the poor compactibility of atomized bronze powder, the authors re-ex-amined the producing process. First powders containing small amounts of sulfur were produced, then, these powders were subjected to oxidation and finally reduced. The powder obtained showed outstanding compactibility in comparison with that of those powders obtained by mixing each component powder. .<BR>The results were summarized as follows:<BR>1. The optimum oxidizing temperature was 800°C.<BR>2. The retained sulfur in the powder decreased with increasing oxidizing time.<BR>3. The optimum reducing temperature after oxidation was 550°C and the reduced cake was crashed easily.<BR>4. Apparent density decreased with increasing sulfur content and oxidizing time.<BR>5. Weight decrease by Rattler test was found in the low percent range and the powder was found excellent in comparison with conventional atomized bronze powders.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- メカニカルアロイング法によるTiC粒子強化チタン基複合材料の創製と引張り特性に及ぼすTiC粒子径の影響
- 酸化物分散強化型フェライト鋼のクリープ挙動
- σ-相合金粉を用いた鉄基粒子分散合金の作製
- TiC生成反応に及ぼすミリング方式の効果
- 真空スクリューディクス式ボールミルによるTiCの合成 : 機械的反応過程
- 超合金MA6000用合金粉のスクリューディスク式ボールミルによる機械的合金化
- Cr-Al-Ti-Ta系合金の粉砕特性
- Ni基合金粉のミリング特性
- 含Cr低合金鋼粉焼結鍛造材の機械的性質に及ぼす焼結条件の影響
- 含Cr低合金鋼粉性質に及ぼす粒子表層多孔質化の影響
- MoSi 2を主体とする発熱体の焼結条件とその性質
- 噴霧法によるCu粉末の製造について
- CrSi2の調製およびその二,三の性質について
- 噴霧黄銅粉の焼結
- 液体噴霧法における噴霧条件について
- 母合金混合法による焼結モネル合金の製造について
- ガス噴霧法による不規則状銅粉の製造
- 粉末圧延法によるモリブデン薄板について
- 冷間圧縮-焼結法によるMoSi2を主体とする電気抵抗発熱体の製造
- MoSi2発熱体の物理的および機械的性質について
- ロール間におけるモリブデン粉末の圧縮成形について
- Liquid Atomizationによる銅系合金粉末の製造
- 噴霧法による多孔質青銅合金粉の製造