Liquid Atomizationによる銅系合金粉末の製造
スポンサーリンク
概要
- 論文の詳細を見る
Atomization appeared to be the best means of obtaining pre-alloved powders without applying a limitation on composition. However, difficulty in the control of particle shapes has restricted the utilization of pre-alloyed powders produced by that process. The investigation has been therefore made on the water atomization of copper alloys, and subsequently the physical properties of the powders and of their pressed compacts were examined.<BR>The results were summarised as follows : -<BR>(1) Molten copper alloys atomized with water become the irregular particles, and this leads to be low apparent density.<BR>(2) To facilitate to produce compacts of high green strength, it may be necessary for atomized bronze and brass powders to be annealed at an adequate temperature.<BR>(3) High rate of cooling velocity developes quenched phase structure in alloys, particularly with alloys such as bronze and Kelmet that has a considerable gap between the liquidus and the solidus. Particles atomized with water show fine quenched phase structures, in comparison with the particles atomized with gas.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 2相ステンレス鋼微粉のスリップキャスティング
- 球状鉄微粉の水噴霧条件および性質
- 真空スクリューディクス式ボールミルによるTiCの合成 : 機械的反応過程
- 超合金MA6000用合金粉のスクリューディスク式ボールミルによる機械的合金化
- Cr-Al-Ti-Ta系合金の粉砕特性
- ワックスを配合したSKH51相当高速度鋼微粉の押出成形
- Ni基合金粉のミリング特性
- 含Cr低合金鋼粉焼結鍛造材の機械的性質に及ぼす焼結条件の影響
- 含Cr低合金鋼粉性質に及ぼす粒子表層多孔質化の影響
- 銅紛性状に及ぼす水噴霧雰囲気の影響
- MoSi 2を主体とする発熱体の焼結条件とその性質
- 焼結ステンレス鋼製造における問題点
- 噴霧法によるCu粉末の製造について
- CrSi2の調製およびその二,三の性質について
- 噴霧黄銅粉の焼結
- 液体噴霧法における噴霧条件について
- 母合金混合法による焼結モネル合金の製造について
- ガス噴霧法による不規則状銅粉の製造
- 粉末圧延法によるモリブデン薄板について
- 冷間圧縮-焼結法によるMoSi2を主体とする電気抵抗発熱体の製造
- MoSi2発熱体の物理的および機械的性質について
- ロール間におけるモリブデン粉末の圧縮成形について
- Liquid Atomizationによる銅系合金粉末の製造
- 噴霧法による多孔質青銅合金粉の製造