CrSi2の調製およびその二,三の性質について
スポンサーリンク
概要
- 論文の詳細を見る
Some basic properties of CrSi<SUB>2</SUB> as a refractory hard material have been investigated. CrSi<SUB>2</SUB> powder was prepared by arc melting of pure chromium and silicon mixture in an argon atmosphere and subsequently crushed by ball mill. This powder was then hot-pressed in vaccum.<BR>The specimens obtained were subjected to various tests, the results of which are summarized as follows.<BR>1 The optimum temperature in hot-pressing of CrSi<SUB>2</SUB> was 1350°C. The density attained 97.0% of the theoretical value.<BR>2 Corrosion resistances to three kinds of dilute acids were superior to any other Disilisides which we had studied.<BR>3 The oxidation resistance at 1200°C was 0.0011g/cm<SUP>2</SUP>/day.<BR>4 Electrical resistance at room temperature was 646×10<SUP>-6</SUP>Ω-cm, 1900×10<SUP>-6</SUP>Ω-cm at 800°C.<BR>5 Thermo electromotive force at room and high temperature was 30 to 60 times higher than that of MoSi2 and TiSi<SUB>2</SUB>.<BR>6 In general, the hardness in hot state decreases with rising temperature. For instance, it was 280 at 800°C.<BR>7 Modulus of rupture at 800°C was 21.3kg/mm<SUP>2</SUP>.<BR>8 The thermal shock resistance of CrSi<SUB>2</SUB> was poor.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 2相ステンレス鋼微粉のスリップキャスティング
- 球状鉄微粉の水噴霧条件および性質
- 真空スクリューディクス式ボールミルによるTiCの合成 : 機械的反応過程
- 超合金MA6000用合金粉のスクリューディスク式ボールミルによる機械的合金化
- Cr-Al-Ti-Ta系合金の粉砕特性
- ワックスを配合したSKH51相当高速度鋼微粉の押出成形
- Ni基合金粉のミリング特性
- 含Cr低合金鋼粉焼結鍛造材の機械的性質に及ぼす焼結条件の影響
- 含Cr低合金鋼粉性質に及ぼす粒子表層多孔質化の影響
- 銅紛性状に及ぼす水噴霧雰囲気の影響
- MoSi 2を主体とする発熱体の焼結条件とその性質
- 焼結ステンレス鋼製造における問題点
- 噴霧法によるCu粉末の製造について
- CrSi2の調製およびその二,三の性質について
- 噴霧黄銅粉の焼結
- 液体噴霧法における噴霧条件について
- 母合金混合法による焼結モネル合金の製造について
- ガス噴霧法による不規則状銅粉の製造
- 粉末圧延法によるモリブデン薄板について
- 冷間圧縮-焼結法によるMoSi2を主体とする電気抵抗発熱体の製造
- MoSi2発熱体の物理的および機械的性質について
- ロール間におけるモリブデン粉末の圧縮成形について
- Liquid Atomizationによる銅系合金粉末の製造
- 噴霧法による多孔質青銅合金粉の製造