鉄―銅合金の焼結に及ぼすA<SUB>3</SUB>変態による不連続粒成長の影響
スポンサーリンク
概要
- 論文の詳細を見る
The sintering of iron-copper (17 vol%) powder compacts has been studied on the basis of the sintering characteristics of iron powder compacts. The sintering was carried out in various heat-treatment programs in which A<SUB>3</SUB> transformation and melting of copper were taken into account. The dilatometric measurements were made during sintering and the microscopic structures were examined on some sintered specimens also. The sintering behaviors of iron-copper (17 vol%) alloy powder were similar to those of iron below the melting point of copper, that is, the discontinuous grain growth at A<SUB>3</SUB>-transformation inhibited farther shrinkage in both α and γ ranges. The discontinuous grain growth also prevented the shrinkage in the presence of liquid copper. This effect was remarkable when the specimen had been pre-sintered in the a range.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 鉄合金の焼結に及ぼす相変態の影響
- 円筒形金型を用いた金属粉体圧縮成形過程における半径方向応力について
- WC-Co合金の研削表面状態に及ぼす焼鈍の効果
- 多孔質焼結体の結晶粒成長に対する残留空げきのピン止め効果
- 鉄―銅合金の焼結に及ぼすA3変態による不連続粒成長の影響
- 金属圧粉体の降伏条件
- 噴霧銅粉およびα-アルミナ粉の三軸圧縮成形
- 金属粉体の三軸圧縮試験
- 液相と伴う焼結現象
- 粉末の焼結現象 (ステンレス鋼粉)
- 三軸圧縮試験法による金属粉体の圧縮特性の測定