三軸圧縮試験法による金属粉体の圧縮特性の測定
スポンサーリンク
概要
- 論文の詳細を見る
Tri-axial compression tests were made on copper, zinc and aluminium powders of specified in particle shapes and sizes under hydrostatic confining pressure up to 360 kg/cm2. By the examination of mechanical behaviours of each powder during compaction, the following results were obtained: The principal stress ratio, σ2/σ1, for each powder showed a nearly constant value during compacting up to the maximum pressure of this test. The ratio depended mainly on the powder material and it increased about 5 and 24% for copper and zinc powders respectively, when 1 wt% of zinc stearate was added as a lubricant. The friction angles calculated from these values were about 43°, 44° and 45°, for aluminium, copper and zinc powders in the unlubricated condition. The change in shearing strength of all powders during compaction could be expressed in the form of Mohr-Coulomb yield criterion.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 熱間における岩石の破壊靱性に関する研究
- 熱衝撃疲労試験による岩石の物性変化の評価に関する研究
- 一軸圧縮下における加熱岩石の力学的挙動
- 岩石の熱疲労-2-
- 鉄合金の焼結に及ぼす相変態の影響
- 円筒形金型を用いた金属粉体圧縮成形過程における半径方向応力について
- WC-Co合金の研削表面状態に及ぼす焼鈍の効果
- 多孔質焼結体の結晶粒成長に対する残留空げきのピン止め効果
- 鉄―銅合金の焼結に及ぼすA3変態による不連続粒成長の影響
- 金属圧粉体の降伏条件
- 噴霧銅粉およびα-アルミナ粉の三軸圧縮成形
- 金属粉体の三軸圧縮試験
- 液相と伴う焼結現象
- 粉末の焼結現象 (ステンレス鋼粉)
- 三軸圧縮試験法による金属粉体の圧縮特性の測定