高純度TiC粉末製造に関する研究(第1報) : TiO<SUB>2</SUB>の真空炭化による微粉TiC製造について
スポンサーリンク
概要
- 論文の詳細を見る
A new process for fine TiC powder of high purity has been studied, which consists of the following two stages:<BR>(1) The mixture of fine TiC powder and free carbon is obtained from the mixture of TiO2 and C (TiO<SUB>2</SUB>:C<1:3). Mixing agent is added for homogeneous dispersion of TiO<SUB>2</SUB> particles.<BR>(2) The carburized lump produced in the first stage is heated with metallic Ca and then treated by dilute acid to remove free carbon.<BR>This paper reports the effects of mixing agents such as castor oil, poly-oxyethylene nonyl phenyl ether, phenol resin (diluted by toluene) and pitch (medium viscosity) on the particle size of the vacuum-carburized products in the stage (1).<BR>These mixing agents were all effective in dispersing TiO<SUB>2</SUB> particles in the mixtures, but the vacuum-carburized products were not always fine. The best result was obtained by using castor oil as mixing agent.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- MA法によって製造されたAl_2O_3分散強化Ni粉の焼結性
- 機械的合金化法を応用したTiC分散強化銅の作製
- メカニカルアロイングを応用して作製したTiCおよびZrC分散強化銅の機械的特性
- 機械的合金化法を応用したアルミナ分散強化銅の作製
- 機械的合金化法を応用した炭化ホウ素分散強化銅の作製
- TiCxOyの標準生成Gibbs自由エネルギーに関する一考察
- Ni-Ti-No-C系に出現する新炭化物相について
- 低酸素領域におけるδ-TiCxOy相の高炭素側相領域
- 反応焼結Cu-TiC-TiB2合金の焼結条件と合金の組織
- 氷晶石系融体の二酸化炭素ガス溶解度の測定
- Cu-Ti-B合金の反応焼結
- アルミニウム青銅の焼結(第2報) : 銅粉とCu-Al合金粉混合圧粉体の焼結
- B_2O_3の炭熱還元によるニッケルホウ化物の製造に関する基礎研究
- 溶浸を応用したハードフェーシングに関する研究(第2報) : TiC/Fe-Mo-C系溶浸合金による耐摩耗層について
- 高硬度材料に関する研究
- 高純度TiCの製造に関する研究(第2報) : Ca処理による粗TiCの精製について
- 高純度TiC粉末製造に関する研究(第1報) : TiO2の真空炭化による微粉TiC製造について
- 起電力法によるNiW2B2の標準生成ギブス自由エネルギーとNi-W2成分系の活量の測定
- Ti3+還元法による銅微粉末の製造
- 溶浸法の発達について
- アルミニウム青銅の焼結(第1報) : 炭素を介在させた減圧下でのCu-Al合金粉末の焼結
- Ni-Ti-O系におけるNi側等温状態図
- 起電力法によるNi3BおよびNi2Bの熱力学的性質について
- 溶浸用Ni-B-Si 3元合金の液相面について
- Ni-B2元系のNi側における状態図について