水噴霧SUS316ステンレス鋼粉の諸特性に及ぼすSi,MnおよびC成分の影響
スポンサーリンク
概要
- 論文の詳細を見る
The main objective of the present work was synthetically to elucidate and evaluate the addition effects of Si, Mn and C on various properties of SUS 316 stainless steel powders produced by water-atomization of liquid metals. The results were summarized as follows:<BR>1) Every component mainly affected particle shapes, the amount of surface oxide and metallographical phase states of powders, where especially Si and Mn gave each other some reverse effects. Consequently, apparent density, compactibility and the like were numerically correlated to Si/Mn ratio.<BR>2) Compressibility was increased when Si: 0.6-0.9% and Mn≤0.2%, because of above-mentioned powder characteristics. On the other hand, for the higher C-content, green density less increased in the stage of plastic deformation of particles.<BR>3) When the powders were vacuum-sintered at temperature below 1200°C, the same Si-component range as<BR>2) gave a maximum sintered density, and also gave a lower activation energy for sintering than any other ranges.<BR>4) The sintering rate and pore-spherodization of compacts were accelerated with increase of Si-content. Therefore, mechanical properties, especially porosity-sensitive ductility were appreciably improved in Si-rich materials which were sintered at higher temperature.<BR>5) Corrosion resistance in boiling acid solutions was complicatedly related to every component, being overlapped by the influence of residual pore shape and oxides along grain boundary. All these sintered materials seemed stronger for boiling 65% HNO<SUB>3</SUB>-solution.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 271 角鋼用蛍光自動探傷装置の開発(試験検査・熱処理, 性質, 日本鉄鋼協会第 77 回(春季)講演大会講演)
- 高密度化ならびにCu, Sn粉プレミックスに伴う焼結ステンレス鋼の密度および耐酸性の変化
- オーステナイト系焼結ステンレス鋼の耐食性について
- ミガキ帯鋼表面キズの超音波自動探傷法
- 快削性電磁けい素鉄
- 非破壊試験法 II
- 非破壊試験法 I
- 角棒鋼に対する螢光磁粉探傷の自動化
- オーステナイト系鋳鋼の超音波探傷
- 15Cr-3Al-Fe系電気抵抗材の研究
- 快削性1%けい素鉄
- 快削電磁純鉄の箱焼鈍
- 異方性アルニコ磁石を用いた接着用磁石体の形状による接着力の変化について
- 160 粉末圧延溶接法の研究(第1報) : TIGアークによる肉盛溶接
- 159 粉末圧延による溶加材の製造
- 快削性電磁純鉄における鉛成分変化の影響
- プラズマ誘導炉溶解パーマロイ合金の特性について
- 17%Cr快削電磁ステンレス(MER2F)帯の諸特性
- Fe-Cr, Fe-NiおよびFe-Ni-Co封着合金の熱膨張係数について
- 粉末圧延による溶加材の製造
- 水噴霧SUS316ステンレス鋼粉の諸特性に及ぼすSi,MnおよびC成分の影響
- ステンレス鋼粉末の試作研究 (ステンレス鋼粉)
- SUS316ステンレス焼結材に及ぼすSi,MnおよびC成分の影響 (ステンレス鋼粉)