17%Cr快削電磁ステンレス(MER2F)帯の諸特性
スポンサーリンク
概要
- 論文の詳細を見る
New free-machining magnetic core stainless steel sheet containing 17% chromium was studied to develop. And the underwritten excellent properties were confirmed as well as good corrosion resistance, machinability and deep drawability.(1) After higher temperature (1200°C) annealing high magnetic properties were achieved as about 0.6 Oe in coercive force and about 6000 in maximum permeability. After proper cold rolling and subsequent annealing, the better magnetic properties were obtained.(2) The electrical resistivity was as high as 75μΩ·cm, and therefore good effective permeability was obtained.This material is suitable for application in alternating magnetic field.
- 大同特殊鋼株式会社の論文
著者
関連論文
- 271 角鋼用蛍光自動探傷装置の開発(試験検査・熱処理, 性質, 日本鉄鋼協会第 77 回(春季)講演大会講演)
- 高密度化ならびにCu, Sn粉プレミックスに伴う焼結ステンレス鋼の密度および耐酸性の変化
- オーステナイト系焼結ステンレス鋼の耐食性について
- ミガキ帯鋼表面キズの超音波自動探傷法
- 快削性電磁けい素鉄
- 非破壊試験法 II
- 非破壊試験法 I
- 角棒鋼に対する螢光磁粉探傷の自動化
- オーステナイト系鋳鋼の超音波探傷
- 15Cr-3Al-Fe系電気抵抗材の研究
- 快削性1%けい素鉄
- 快削電磁純鉄の箱焼鈍
- 異方性アルニコ磁石を用いた接着用磁石体の形状による接着力の変化について
- 160 粉末圧延溶接法の研究(第1報) : TIGアークによる肉盛溶接
- 159 粉末圧延による溶加材の製造
- 快削性電磁純鉄における鉛成分変化の影響
- プラズマ誘導炉溶解パーマロイ合金の特性について
- 17%Cr快削電磁ステンレス(MER2F)帯の諸特性
- Fe-Cr, Fe-NiおよびFe-Ni-Co封着合金の熱膨張係数について
- 粉末圧延による溶加材の製造
- 水噴霧SUS316ステンレス鋼粉の諸特性に及ぼすSi,MnおよびC成分の影響