高密度YBa<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>x</SUB>超伝導セラミクスの作製と特性 : 19881128
スポンサーリンク
概要
- 論文の詳細を見る
The effects of pore structure on the superconducting properties of dense YBa<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>x</SUB> ceramics were investigated. The dense samples, 6.20 g/cm<SUP>3</SUP>, with many of small pores were prepared using a high calcining temperature (940°C), a planetary milling for a long time (24h) and ordinary sintering at low temperature (900°C) for 60h. The dense samples with the small pores showed larger pore-surface than the porous samples with large pores. Therefore, the dense sample facilitated the diffusion of oxygen within the material during the sintered processing, and it has become the orthorhombic structure. The resistivity and the critical current density of the dense samples increased about twice of that of the normal density samples.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- P1-29 BLTトランスデューサーを用いた高温ガス測定(ポスターセッション1(概要講演))
- 解説 タングステンブロンズ型PbNb2O6セラミクス--低Qm圧電素子への応用
- F-1 PbNb_2O_6を用いた高温用超音波トランスデューサの製作
- 透明セラミックを用いた音圧センサ
- PB25 PLZT圧電セラミックの複屈折の音圧特性(ポスターセッションB)
- ホットプレスしたチタン酸ビスマスセラミックスの粒子配向と電気的性質
- 圧電セラミックスの圧電特性及び電界誘起歪に及ぼす添加物の影響
- 圧電セラミックスにおける電界誘起歪の電界強度依存性
- ホットプレスしたYBa_2Cu_3O_x超伝導セラミックスの特性
- 超伝導YBa2Cu3Oxセラミクスの諸特性と空孔構造 (酸化物超伝導物質と材料) -- (〔粉体粉末冶金協会〕昭和63年度春季大会講演特集)