異方性ランタン系フェライト磁石の磁気特性
スポンサーリンク
概要
- 論文の詳細を見る
Experiments were carried out to investigate the effect of CaO substitution on some properties of anisotropic La ferrite magnets. It was confirmed that the substitution of CaO to La<SUB>2</SUB>O<SUB>3</SUB> contributes to formation of the magnetoplumbite structure, and these La-Ca ferrites have excellent properties as a permanent magnet. Compositions were chosen according to the formula (La<SUB>2</SUB>O<SUB>3</SUB>)<SUB>1-x</SUB>(2CaO)<SUB>x</SUB>⋅nFe<SUB>2</SUB>O<SUB>3</SUB>, where X was varied between 0 and 1.0, and n between 12 and 6. The optimum conditions of making magnet and some properties of a typical sample are the following: chemical analysis composition La<SUP>3+</SUP><SUB>0.501</SUB>Ca<SUP>2+</SUP><SUB>0.697</SUB> Fe<SUP>2+</SUP><SUB>0.212</SUB>Fe<SUP>3+</SUP><SUB>11.558</SUB>O<SUB>19</SUB>, S.S.C.: 1300°C×1 h in O<SUB>2</SUB>, S.C.: 1250°C×0.5h in O<SUB>2</SUB>, Jm=0.45T, Jr=0.43T, H<SUB>CJ</SUB>=170.0 kA/m, H<SUB>CB</SUB>=167.0 kA/m, (BH)<SUB>max</SUB>=35.0 kJ/m3, H<SUB>A</SUB>=1544kA/m, K<SUB>A</SUB>=3.47×10<SUB>5</SUB> J/m<SUP>3</SUP>, σs=86.6×10<SUP>-6</SUP> Wb⋅m/kg, D=5.05 Mg/m<SUP>3</SUP>.
著者
関連論文
- FePt微粒子および集積膜の磁気特性
- 化学合成による部分的規則化Fe-Pt微粒子の構造と磁性
- 化学合成による部分的規則化Fe-Pt微粒子の構造と磁性(高密度磁気ストレージ材料 : 開発の現状・未来と解析技術)
- 異方性ランタン系フェライト磁石の磁気特性
- 半硬質磁性材料とその応用
- 粉末冶金法によるFe-Si-Al三元系合金とそれらの電磁気的性質
- 異方性Ca-La-Nd系フェライト磁石の諸特性
- 等方性Ca系フェライト磁石の諸性質
- 粉末冶金法によるFe-W-Co-Cr-Mo系合金の磁気特性
- 粉末冶金法によるFe-W-Cr-Mo系半硬質磁性材料の磁気特性
- 粉末冶金法による(Ce-MM)-Co-Cu系合金の磁気特性
- 粉末式溶射法によるFe-Si-Al三元系合金シートの電磁気的性質並びにそれらのオーディオヘッドコアとしての適用性
- 放電焼結法によるセンダストシートの製造並びにそれらの電磁気的性質
- センダスト合金の粉末圧延法とそれらの電磁気的特性
- (Pr, Dy)-(Fe, Co)-B系急冷薄帯磁石の磁気特性並びにそれらのボンド磁石の磁気特性
- 異方性Caフェライト磁石の磁気特性に及ぼすストロンチウム酸化物置換の影響
- 等方性Ba-Zn-Al-La系W型6方晶フェライト磁石の磁気特性