粉末冶金法によるFe-Si-Al三元系合金とそれらの電磁気的性質
スポンサーリンク
概要
- 論文の詳細を見る
The author reported previously the manufacturing of Sendust alloy sheets by powder rolling or electric discharge sintering process.<BR>So far as magnetic properties are concerned, the products are slightly inferior to the Sendust alloy melted, owing to the fact that the density of these samples is lower than that of the latter, and also to the fact that their chemical compositions were not controlled correctly.<BR>In this experiment, the author examined some properties of sintered Sendust-alloys without or with the addition of phosphorous and titanium. Materials used were mother alloy-(6.4% Al, 11.71% Si, Fe balanced), electrolytic iron-, carbonyl iron-, red-phosphorous-, ferro-phosphorous-and ferro-titanium-powders.<BR>The compacts of the Sendust alloy (5.3% Al, 9.7% Si, Fe balanced) were obtained by pressing the mixture of 83% mother alloy and 17% iron-powders. In these compacts, the electrolytic iron powder was found to be a better binder than the carbonyl iron powder.<BR>Sintered Sendust-alloys showed the following excellent properties. But the effects of the addition of P and Ti were not so remarkable.<BR>Effective permeability of sintered Sendust alloy sheets (0.71mm thick) was higher than that of Alperm sheets (0.6mm thick).<BR>The Sendust sheet will be more superior to the Alperm sheet for the same thickness, since the frequency characteristic depends on the thickness. Electro-magnetic and physical properties of a typical sample are as follows : Um=20000, <SUB>B</SUB>H<SUB>C</SUB>=0.08 Oersted : Br=1900 Gauss : B<SUB>10</SUB>=7300 Gauss : D=6.49g/cm3 : ρ=133 μΩ-cm : Hv=496. This sample was sintered at 1150°C for 3hr in vacuum.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- FePt微粒子および集積膜の磁気特性
- 化学合成による部分的規則化Fe-Pt微粒子の構造と磁性
- 化学合成による部分的規則化Fe-Pt微粒子の構造と磁性(高密度磁気ストレージ材料 : 開発の現状・未来と解析技術)
- 異方性ランタン系フェライト磁石の磁気特性
- 半硬質磁性材料とその応用
- 粉末冶金法によるFe-Si-Al三元系合金とそれらの電磁気的性質
- 異方性Ca-La-Nd系フェライト磁石の諸特性
- 等方性Ca系フェライト磁石の諸性質
- 粉末冶金法によるFe-W-Co-Cr-Mo系合金の磁気特性
- 粉末冶金法によるFe-W-Cr-Mo系半硬質磁性材料の磁気特性
- 粉末冶金法による(Ce-MM)-Co-Cu系合金の磁気特性
- 粉末式溶射法によるFe-Si-Al三元系合金シートの電磁気的性質並びにそれらのオーディオヘッドコアとしての適用性
- 放電焼結法によるセンダストシートの製造並びにそれらの電磁気的性質
- センダスト合金の粉末圧延法とそれらの電磁気的特性
- (Pr, Dy)-(Fe, Co)-B系急冷薄帯磁石の磁気特性並びにそれらのボンド磁石の磁気特性
- 異方性Caフェライト磁石の磁気特性に及ぼすストロンチウム酸化物置換の影響
- 等方性Ba-Zn-Al-La系W型6方晶フェライト磁石の磁気特性