Pを添加したCu-Sn系含油軸受用合金の焼結現象と高荷重下での軸受運転性能について
スポンサーリンク
概要
- 論文の詳細を見る
Effects of the addition of phosphorus (0.2-0.8%) to Cu-9% Sn compacts which was standard composition of conventional bronze oil impregnated sintered bearings were examined during sintering process. The bearing running test was also carried out under the heavy load condition for Cu-base oil impregnated bearings on Cu-9%Sn-0.4%P bearing.<BR>The results obtained were as follows;<BR>1) By the addition of phosphorus, Cu-Sn compacts were remarkably strengthened. For example, the radial crushing strength of the compact added 0.4% phosphorus, pressed at 2 t/cm<SUP>2</SUP> and sintered at 700°C for 30 min., was 11 kg/mm<SUP>2</SUP> higher than that of the non-phosphorus compact.<BR>2) On the case of addition of phosphorus above 0.4%, the swelling phenomena during sintering process, which occur above peritectic temperature (798°C) in ordinary mixed Cu-Sn powder compacts were not observed. The reason was seemed that owing to the addition of phosphorus alloying of Sn had progressed sufficiently through the sintering below peritectic temperature.<BR>3) Sinterability of mixed Cu-Sn powder compacts was extremely enhanced by the addition of phosphorus. With the progress of sintering, large pores became larger, but on the contrary small pores became smaller and gradually disappeared. So, the oil impregnated sintered Cu-Sn-P bearings having large size pores and high strength can be produced by selecting the proper sintering conditions.<BR>4) In the running test, Cu-9%Sn-0.4%P bearings showed excellent bearing performance even under the heavy load condition (P=20 kg/cm<SUP>2</SUP>, N=4, 000 rpm, PV=2, 000 kg/cm<SUP>2</SUP>m/min) in which the oil impregnated pores were closed by the plastic flow of the rubbing surface in the conventional sintered Cu-9%Sn bearings.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 729 プラズマビーム遠心アトマイズ法によるチタン合金粉末の製造とその特性(チタン (1), 萌芽・境界技術, 日本鉄鋼協会第 109 回(春季)講演大会)
- 焼結鋼と炭素鋼の摩擦圧接
- 118 焼結鋼とS25C鋼の摩擦圧接(第2報)
- チタン合金の超塑性 (超塑性材料とその加工技術)
- 討 37 チタン系材料の超塑性と加工(V 最近の超塑性利用技術, 第 110 回講演大会討論会講演概要)
- 焼結耐熱合金(その2)
- 焼結耐熱合金(その1)
- 「金属加工技術」 : 機械設計者と金属加工技術者の対話
- 焼結材料(摩擦材料シリ-ズ)
- チタン合金部品の粉末成形 (最近の生産加工技術) -- (難加工材の成形と被覆)
- P-18 ガリウム練成充填材の開発研究 : 5.生理食塩水中および乳酸溶液中への構成元素の溶出および組織構造
- ガリウム錬成充填材における操作性の検討 : 1.エチルアルコール加ムリングによる練和物親和性の抑止
- P-19 ガリウム練成充填材の開発研究 : 6.合金粉末の粒度配合比と物性
- B-5 ガリウム練成充填材の開発研究 : 4.合金粉末粒度と物性
- P-2 ガリウム練成充〓材の開発研究 : 3.固体ガリウム-合金粉末方式における練和法と物性
- P-1 ガリウム練成充〓材の開発研究 : 2.組織構造の検討
- 焼結鍛造により得られたSKH51種相当高速度工具鋼の機械的特性
- 高速回転用青銅系焼結含油軸受の開発
- W-Mo-Ni-Fe系焼結合金の機械的特性に与える焼決条件および焼処理の影響
- 焼結含油軸受の使用限界PV値の測定について
- 鉄-銅-炭素および鉄-銅-りん-炭素系焼結合金の焼結時の寸法変化と二,三の機械的性質について
- 焼結含油軸受の高速運転時の潤滑に関する二,三の様相 : 特に起動時の様相と個体潤滑剤の挙動
- Cu-Sn-P-MoS2系焼結含油軸受の製造
- Pを添加したCu-Sn系含油軸受用合金の焼結現象と高荷重下での軸受運転性能について
- Cu-Sn-P-MoS2系焼結含油軸受の高速運転性能 : 特にMoS2粒子周囲のバインダ相の効果について
- 鉛および黒鉛を多量に添加した青銅系焼結含油軸受の試作と二,三の軸受性能
- 焼結含油軸受の低荷重高速度領域での潤滑機構に関する二,三の様相(第2報) : 低粘度潤滑油を用いた場合
- 焼結含油軸受の低荷重高速度領域での潤滑機構に関する二,三の様相(第1報) : 高粘度潤滑油を用いた場合
- Ti合金粉末HIP材の超塑性鍛造