焼結鍛造により得られたSKH51種相当高速度工具鋼の機械的特性
スポンサーリンク
概要
- 論文の詳細を見る
High speed steels (JIS SKH51) have been produced by sinter forging using high-pressure water atomized powders ( ?? 10μm). The mechanical properties such as bend strength and hardness have been measured and optical and electron microscopic observation have been carried out. The properties of the forged steels have been compared with those of conventional sinterd steels. The results obtained can be summarized as follows:<BR>1) The grain of sinter-forged high speed steels is very fine and carbides ( ?? 1μm) distributed uniformly are observed.<BR>2) Carbide particle size is dependent upon powder size and sintering temperature, but not upon austenitizing temperature.<BR>3) Bend strength of sinter forged steels is 450kg/mm2, whereas that of conventional products is 200kg/mm<SUP>2</SUP>.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 338 Fe-Cu-C系焼結鋼板と炭素鋼棒の摩擦圧接
- 焼結鋼と炭素鋼の摩擦圧接
- 焼結材料(摩擦材料シリ-ズ)
- P-18 ガリウム練成充填材の開発研究 : 5.生理食塩水中および乳酸溶液中への構成元素の溶出および組織構造
- ガリウム錬成充填材における操作性の検討 : 1.エチルアルコール加ムリングによる練和物親和性の抑止
- P-19 ガリウム練成充填材の開発研究 : 6.合金粉末の粒度配合比と物性
- B-5 ガリウム練成充填材の開発研究 : 4.合金粉末粒度と物性
- P-2 ガリウム練成充〓材の開発研究 : 3.固体ガリウム-合金粉末方式における練和法と物性
- P-1 ガリウム練成充〓材の開発研究 : 2.組織構造の検討
- Cu-Al合金粉の酸化-還元による2段階焼結に関する研究(第2報) : 還元工程
- Cu-Al合金粉の酸化-還元による2段階焼結に関する研究(第1報) : 酸化工程
- 粉末鍛造法による急冷凝固アルミニウム合金部材の製造およびその評価
- アルミニウムを含む粉末の焼結に及ぼす焼結助剤添加の効果
- 焼結鍛造により得られたSKH51種相当高速度工具鋼の機械的特性
- 高速回転用青銅系焼結含油軸受の開発
- W-Mo-Ni-Fe系焼結合金の機械的特性に与える焼決条件および焼処理の影響
- 焼結含油軸受の使用限界PV値の測定について
- 鉄-銅-炭素および鉄-銅-りん-炭素系焼結合金の焼結時の寸法変化と二,三の機械的性質について
- 焼結含油軸受の高速運転時の潤滑に関する二,三の様相 : 特に起動時の様相と個体潤滑剤の挙動
- Cu-Sn-P-MoS2系焼結含油軸受の製造
- Pを添加したCu-Sn系含油軸受用合金の焼結現象と高荷重下での軸受運転性能について
- Cu-Sn-P-MoS2系焼結含油軸受の高速運転性能 : 特にMoS2粒子周囲のバインダ相の効果について
- 鉛および黒鉛を多量に添加した青銅系焼結含油軸受の試作と二,三の軸受性能
- 焼結含油軸受の低荷重高速度領域での潤滑機構に関する二,三の様相(第2報) : 低粘度潤滑油を用いた場合
- 焼結含油軸受の低荷重高速度領域での潤滑機構に関する二,三の様相(第1報) : 高粘度潤滑油を用いた場合