焼結Cr-Mo鋼の変態特性
スポンサーリンク
概要
- 論文の詳細を見る
A study has been made on the transformation features of sintered Cr-Mo steels (Fe-1%Cr-0.2%Mo-0.35%C) made from premixed powders. Metallic Mo powder or Mo carbide powder (Mo<SUB>2</SUB>C) was added to an atomized iron powder together with graphite and Cr carbide powders. The powder mixtures were pressed at 6 t/cm<SUB>2</SUB>, and sintered at 1250°C in vacuum (10<SUB>-4</SUB> mmHg) for 1 hr. The CCT diagrams and the microstructures of these specimens were compared with those made from prealloyed atomized powder.<BR>The results obtained are as follows;<BR>1) The specimens made from premixed powders formed pores caused by liquid phase formation, and the<BR>pores were surrounded by Mo segregated area.<BR>2) The CCT diagrams of those materials moved to shorter cooling time compared with those made from prealloyed powder.<BR>3) In the specimen which contained Mo carbide powder instead of metallic Mo powder, the critical cooling rate was not improved, but the region of bainite formation was extended to longer cooling time.<BR>Above-mentioned results showed that the Mo carbide was relatively effective for the purpose of homogenization.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 鉄−モリブデン−炭素混合圧粉体の焼結過程 : 焼結鋼におけるモリブデンの拡散合金化過程(II)
- 鉄-モリブデン-炭素系圧粉体拡散対における合金化過程 : 焼結鋼におけるモリブデンの拡散合金化過程(I)
- 静的引張試験における焼結炭素鋼の破壊挙動
- 焼結炭素鋼の疲れ破壊挙動
- 焼結Cr-Mo鋼の変態特性に及ぼすMo量およびC量の影響
- フェロモリブデン添加による焼結Cr-Mo鋼の変態特性
- 焼結Cr鋼の窒化層
- 焼結Cr-Mo鋼の機械的性質
- 焼結Cr-Mo鋼の変態特性
- 焼結鋼の気孔組織 : その顕出方法
- 焼結Cr鋼の変態特性について
- 溶浸を応用したハードフェーシングに関する研究(第2報) : TiC/Fe-Mo-C系溶浸合金による耐摩耗層について
- 溶浸用Ni-B-Si 3元合金の液相面について
- ホットプレスアルミナのクリープにおける選択方位の変化とその影響