焼結Cr鋼の変態特性について
スポンサーリンク
概要
- 論文の詳細を見る
Using three kinds of Cr containing powders, vacuum sintered Cr-steel specimens of different porosity were prepared. The transformation behavior and hardenability of these specimens were investigated by means of dilatometric method. The results obtained are as follows:<BR>1) The difference of porosity had no effect on the feature of CCT diagram and the critical cooling rate.<BR>2) Different features of CCT diagram were mainly due to the Cr distribution caused by the use of different Cr containing powders.<BR>3) From the relation between critical cooling rate and ideal critical diameter after Grossmann, it was concluded that the hardenability of sintered steels was not inferior to that of wrought steels in the experimental conditions of present investigation.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 鉄−モリブデン−炭素混合圧粉体の焼結過程 : 焼結鋼におけるモリブデンの拡散合金化過程(II)
- 鉄-モリブデン-炭素系圧粉体拡散対における合金化過程 : 焼結鋼におけるモリブデンの拡散合金化過程(I)
- 静的引張試験における焼結炭素鋼の破壊挙動
- 焼結炭素鋼の疲れ破壊挙動
- 焼結Cr-Mo鋼の変態特性に及ぼすMo量およびC量の影響
- フェロモリブデン添加による焼結Cr-Mo鋼の変態特性
- 焼結Cr鋼の窒化層
- 焼結Cr-Mo鋼の機械的性質
- 焼結Cr-Mo鋼の変態特性
- 焼結鋼の気孔組織 : その顕出方法
- 焼結Cr鋼の変態特性について
- 溶浸を応用したハードフェーシングに関する研究(第2報) : TiC/Fe-Mo-C系溶浸合金による耐摩耗層について
- 溶浸用Ni-B-Si 3元合金の液相面について
- ホットプレスアルミナのクリープにおける選択方位の変化とその影響