Reaction behavior of slag and spinel in steel ladle castables
スポンサーリンク
概要
- 論文の詳細を見る
The difference in corrosion behavior between alumina-spinel and alumina-magnesia castables in a steel slag was investigated with emphasis on the composition of spinel phase. The spinel primarily-added to the alumina-spinel castable had the stoichiometric composition, whereas the spinel forming secondarily in the alumina-magnesia castable was in an alumina-rich composition. The model reaction between sintered spinel and slag revealed that the stoichiometric spinel was highly wettable to slag and the molten slag deeply penetrated into the sintered body. In contrast, the alumina-rich spinel was less wettable. It was found that the alumina-rich spinel changed into stoichiometric one at the interface between spinel and slag, and that an iron-alumina spinel formed following to dissolution of the excessive alumina into slag. The increase in alumina content seemed to increase the viscosity of the slag, leading to retardation of penetrative wetting of slag to the alumina-rich spinel.
- 公益社団法人 日本セラミックス協会の論文
著者
-
Hojo Junichi
Department of Applied Chemistry, Faculty of Engineering, Kyushu University
-
ENOMOTO Naoya
Department of Applied Chemistry, Faculty of Engineering, Kyushu University
-
Hojo Junichi
Department Of Applied Chemistry Faculty Of Engineering Kyushu University
-
Enomoto Naoya
Department Of Applied Chemistry Faculty Of Engineering Kyushu University
-
SADATOMI Yoshitaka
Technical Research Laboratories, Krosaki Harima Corporation
-
Hojo Junichi
Department Chemistry & Biochemistry, Graduate School of Engineering, Kyushu University
関連論文
- Effect of AlN additive on densification, microstructure and strength of liquid-phase sintered SiC ceramics by spark plasma sintering
- Synthesis and characterization of TiO2-coated SiO2 particles by hydrolysis of titanium alkoxide in alcohol solvents
- Nanostructured silicon carbide ceramics fabricated through liquid-phase sintering by spark plasma sintering
- Synthesis of Ca3Sc2Si3O12:Ce3+ phosphor via newly developed emulsion route
- LiAlH4とダイヤモンド表面のカルボキシル基の化学反応
- Preparation of Novel Hollow Fiber Silica Using Collagen Fibers as a Template
- 01-P-16 Effect of Surface Treatments on Dispersibility and EPD Behavior of Fine SiC Powder in Aqueous Suspensions
- 01-P-12 Microwave Synthesis of TiO_2 Nanoparticles in Self-Hydrolysis Process
- Research Development of New Technologies for Social Foundation
- Template Effect of Cholesterol-based Organogels on Sol-Gel Polymerization Creates Novel Silica with a Helical Structure
- Evidence for the Importance of a Cationic Charge in the Formation of Hollow Fiber Silica from an Organic Gel System
- Nanostructure control of liquid-phase sintered Si3N4 ceramics by spark plasma sintering
- Synthesis of rutile TiO_2 with high specific surface area by self-hydrolysis of TiOCl_2 in the presence of SDS
- Effect of ultrasonication on anodic oxidation of titanium(Aqueous Solution Science for Ceramic Processing II)
- Thermal Stress Analysis of Multilayer Composite of SiC-TiC-Ni System (傾斜機能材料)
- Reaction behavior of slag and spinel in steel ladle castables
- Microstructure and Properties of Cermets Obtained from Ni-Plated TiC Composite Particles (高次制御材料-1-)
- Preparation of Metal-Coated Ceramics Particles by Agglomeration Coating Technique
- Development of Industrial Process for Fly-Ash Zeolite Production by Microwave Irradiation
- Synthesis and photocatalytic activity of small brookite particles by self-hydrolysis of TiOCl2
- Metal plating via electrochemical reduction of oxide layers formed by electrophoretic deposition
- Evaluation on microstructure and dissolution behavior of SiC-AlN composites fabricated by SPS process
- Morphological Control to Kneed Gold Nanowire through Initial Mixing in Polyol Process
- A Novel Method to Synthesize Monodispersed Magnetite Nanoparticles
- Change of Morphology during Heating of Amorphous Composite Powder in Si3N4-BN System (特集 アモルファス・ナノ結晶制御と高機能材料)
- Liquid Phase Immunoassay Using Magnetic Markers and Superconducting Quantum Interference Device
- Size Distribution of Magnetic Marker Estimated from AC Susceptibility in Solution for Biosensor Application
- Microstructure and Mechanical Properties of Sintered Bodies of Fine Powders in Si3N4-TiN System (特集 セラミックスのケミカルプロセッシング)
- Microstructure and Properties of MoSi2 and MoSi2-SiC Sintered Bodies Obtained from Fine Powders (金属間化合物の粉末冶金と諸物性)
- Sintering of Ni Powder-Coated Al2O3 Particles and Metal Infiltration into the Porous Sintered Body (高次制御材料-1-)
- Solid Electrochemical Micromachining Using a Tungsten Microelectrode Coated with a Polymer Electrolyte
- Corrosion resistance of alumina-magnesia castable to slag in steel ladle lining
- Photovoltaic Properties of TiO_2-ZnO Composite Electrodes for Dye-Sensitized Solar Cells
- Distribution and Solubility Limit of Al in Al2O3-Doped ZnO Sintered Body
- S16. Sono/Photo Synergy Effect Using TiO_2-coated Fibers and 2.4 MHz Ultrasound(Oral Presentation)
- S1-1 Ultrasound and Ceramic Nanoparticles(Symposium (1) Sonochemical Innovation in Materials Processing)
- P-9 Sonochemical Synthesis of the Silica-coated Magnetite Composite by using ca.30nm Particles(Poster Presentations)