Asymptotic Characteristic of Exact Distribution of Fracture Strength Based on Gamma Distribution as Initial Flaw Size Distribution
スポンサーリンク
概要
- 論文の詳細を見る
In this paper, an exact distribution of fracture strength was derived from extreme value statistics for an initial distribution of flaw size, via conversion to an exact distribution of largest flaw size. Gamma distribution was shown as a better function to approximate the initial distribution data measured by immersion liquid technique. The exact distribution of fracture strength was obtained as a function of the number of links in the weakest link theory. With increasing the number of links, the exact distribution gradually became linear on Weibull plot, and almost coincided to Weibull distribution at the number of links larger than 1000. Compared to actual distributions of fracture strength, the number of links in the specimens was estimated to be in the range from 104 to 105. The above discussion showed a verification of this theory.
- 一般社団法人 日本機械学会の論文
著者
-
Yasuda Kouichi
Department Of Metallurgy And Ceramics Science Faculty Of Engineering Tokyo Institute Of Technology
-
Shiota Tadashi
Department Of Material And Life Science Graduate School Of Engineering Osaka University
-
Wakabayashi Chisato
Department Of Metallurgy And Ceramics Science Graduate School Of Science And Engineering Tokyo Institute Of Technology
-
SHIOTA Tadashi
Department of Metallurgy & Ceramics Science, Tokyo Institute of Technology
-
WAKABAYASHI Chisato
Department of Metallurgy & Ceramics Science, Tokyo Institute of Technology
関連論文
- Effect of Low-Energy Ion Bombardment upon Field-Stimulated Exoelectron Emission from Tungsten Surfaces
- Photon emission during fracture of engineering ceramics and glasses(The 62th CerSJ Awards for Academic Achievement in Ceramic Science and Technology)
- Synthesis of a Biologically Active Fluorescent Derivative of GM1,a Main Ginseng Saponin Metabolite Formed by Intestinal Bacteria
- Theory of Non-destructive Inspection of Ceramics Damaged Through Machining Process
- Availability of gamma distribution as initial distribution of flaw size
- Influence of β-tricalcium phosphate dispersion on mechanical properties of hydroxyapatite ceramics
- 237 Theory of Non-destructive Inspection of Ceramics Damaged through Machining Process
- Asymptotic Characteristic of Exact Distribution of Fracture Strength Based on Gamma Distribution as Initial Flaw Size Distribution
- Bending Strength Dependence of Fractoluminescence Intensity in Silica Glass, Single Crystal and Polycrystalline MgO