SUS-316ステンレス鋼中へのトリチウムガスの溶解速度に対する酸化膜の影響
スポンサーリンク
概要
- 論文の詳細を見る
Characterization of surface impurities on SUS-316 stainless steel was performed with an Auger electron spectroscopy, the surface of which was prepared in two ways. Oxygen impurity was not observed on the surface annealed at 1273K in vacuum but segregation of appreciable amount of sulfur was observed.A duplex oxide layer of chromium and iron oxides was observed on the surface exposed to air at room temperature after vacuum annealing. Summarizing these experimental results and the data of our previous experiment on measurement of dissolution rate of gaseous tritium into the present stainless steel, the barrier effect of oxide film on the dissolution rate of gaseous tritium into stainless steel was discussed. The disappearance of barrier effect of the present duplex oxide film under a reducing conditions was ascribed to the reconstruction of oxide film resulted from the reduction of top layer of iron oxide.
- 九州大学大学院総合理工学研究科,Interdisciplinary Graduate School of Engineering Sciences, Kyushu Universityの論文
- 1992-06-01
著者
関連論文
- RF-放電重水素プラズマの解離度測定とニッケル膜中のプラズマ駆動透過の律速過程
- プラズマ駆動透過実験装置の製作と重水素プラズマのニッケル膜透過挙動
- XPSによるジルカロイ自然酸化膜中におけるSnの化学状態の研究
- Ni(111)面上に吸着した硫黄の拡散係数の測定
- 乾式貯蔵条件下における燃料被覆管内の水素の再分布とその機械的性質への影響
- トリチウムオートラジオグラフィによるSi添加PC鋼棒中の水素分布の可視化
- 総合理工学府におけるFD : 教官による講義相互参観
- オージェ電子分光および接触電位差法によるジルコニウムの酸化機構の研究
- トリチウムオートラジオグラフィによる焼戻しマルテンサイト組織の水素分布の観察
- トリチウムミクロオートラジオグラフィーによるジルカロイ -2 中の水素分布の観察
- SUS-316ステンレス鋼中へのトリチウムガスの溶解速度に対する酸化膜の影響
- 高周波放電水素プラズマによるニッケル表面の不純物の変化とプラズマ駆動透過に及ぼす表面不純物の影響
- Role of Intermetallic Precipitates in Hydrogen Uptake of Zircaloy-2