Initial stage of localized corrosion in artificial pits formed with photon rupture on Zn-5 mass% Al alloy-coated steel
スポンサーリンク
概要
- 論文の詳細を見る
The photon rupture method, by which oxide film and metal are removed by focused pulsed Nd–YAG laser beam irradiation, was applied to form artificial micro-pits in Zn–5 mass% Al alloy-coated steel. The zinc alloy-coated layer was removed by pulsed laser irradiation treatment for about one second in a neutral buffer solution with NaCl. The rest potential transient with the laser treatment was measured. In the early stage of the laser treatment the rest potential of zinc alloy-coated steel changed to the negative direction immediately after every irradiation of a laser pulse and then returned to the previous value. However, after the steel substrate was exposed to the solution, the rest potential moved to the positive direction immediately after every irradiation of a laser pulse and then returned to the previous value. The amplitude and duration of the potential change after the laser irradiation increased with repetition of laser irradiation, related to the pit depth and the exposed area ratio of coated layer/steel substrate. The rest potential fluctuation difference can be explained by galvanic reaction change in the artificial pit formed by laser irradiation on the Zn alloy-coated steel.
- Elsevierの論文
著者
-
TAKAHASHI Hideaki
Asahikawa National College of Technology
-
Uchida Yoshiyuki
Graduate School Of Engineering Hokkaido University
-
Takahashi Hideaki
Graduate School Of Engineering Hokkaido University
関連論文
- Corrosion of Al-Sn-Bi alloys in alcohol at high temperatures. Part I: Effects of the metallurgical structure of the alloys and the metal salt additions to alcohol
- Metallization of Oxide/Hydroxide Film of Aluminum : the Palladium Activation Techniques
- Analysis of the Initial Stage of Localized Corrosion on Zn and Zn Alloy Coated Steels by Photon Rupture Method
- Corrosion of Al–Sn–Bi alloys in alcohols at high temperatures. Part II: Effect of anodizing on corrosion
- Age-Related Changes in Physical Function in Community-Dwelling People Aged 50-79 Years
- Growth of porous type anodic oxide films at micro-areas on aluminum exposed by laser irradiation
- Influence of Zinc Ions on Initial Stage of Localized Corrosion of Zn and Zn-Al Alloy Coated Steels with Photon Rupture Method
- Microfabrication of an anodic oxide film by anodizing laser-textured aluminium
- Initial stage of localized corrosion in artificial pits formed with photon rupture on Zn-5 mass% Al alloy-coated steel
- Initial Stage of Localized Corrosion in Artificial Pits Formed with Photon Rupture on 55mass%Al-Zn Coated Steels
- ゾル・ゲルコーティングとアノード酸化によるAl-(Zr,Si and BaTiO3)複合酸化物皮膜の生成--新規な高性能アルミニウム電解コンデンサの開発を目指して
- ゾル・ゲル法によりZr酸化物を被覆したアルミニウムのアノード酸化(1)アノード酸化皮膜の成長に及ぼす被覆加熱処理の影響
- A perspective on a potential for East Asian Linkage in distance higher education
- Fabrication of Cu Micro-rods with Co-axial Dual Capillary Solution Flow Type Droplet Cell and Electrodeposition with the Cell
- Nb2O5 Deposition on Aluminum from NbCl5-used Sol and Anodizing of Nb2O5-coated Al
- Micro- and Nano-Technologies Based on Anodizing of Aluminum—Combination of Laser Irradiation with Electrochemical Process